Polycarbonate resin composition and molded product thereof

ABSTRACT

A polycarbonate-based resin composition, including: a polycarbonate-based resin satisfying requirements (1) and (2); and a styrene-based resin blended into the polycarbonate-based resin, wherein a ratio of the polycarbonate-based resin in 100 mass % of a total amount of the polycarbonate-based resin and the styrene-based resin is from 50 mass % or more to 99 mass % or less: (1) the polycarbonate-based resin contains a polycarbonate-polyorganosiloxane copolymer containing a polycarbonate block formed of a specific repeating unit and a polyorganosiloxane block containing a specific repeating unit, and an aromatic polycarbonate-based resin except the polycarbonate-polyorganosiloxane copolymer; and (2) the polycarbonate-based resin has a structure in which a domain containing the polyorganosiloxane block is present in a matrix containing the aromatic polycarbonate-based resin as a main component, and a domain containing at least one selected from a block derived from the aromatic polycarbonate-based resin and the polycarbonate block is present inside the domain.

RELATED APPLICATIONS

The present application claims priority under 37 U.S.C. § 371 to International Patent Application No. PCT/JP2018/007887, filed Mar. 1, 2018, which claims priority to and the benefit of Japanese Patent Application Nos. 2017-038838, filed on Mar. 1, 2017, and 2017-240863, filed on Dec. 15, 2017. The contents of these applications are hereby incorporated by reference in their entireties.

TECHNICAL FIELD

The present invention relates to a polycarbonate-based resin composition including a polycarbonate-polyorganosiloxane copolymer, and a molded article of the composition. Specifically, the polycarbonate-based resin composition of the present invention includes a plurality of kinds of resins.

BACKGROUND ART

A polycarbonate-polyorganosiloxane copolymer (hereinafter sometimes abbreviated as “PC-POS copolymer”) has been attracting attention because of its excellent properties, such as high impact resistance, chemical resistance, and flame retardancy. Accordingly, the polycarbonate-polyorganosiloxane copolymer has been expected to be widely utilized in various fields, such as the field of electrical and electronic equipment and the field of automobiles. In particular, the utilization of the polycarbonate-polyorganosiloxane copolymer in casings for a cellular phone, a mobile personal computer, a digital camera, a video camera, an electric tool, a communication base station, a battery, and the like, and in other commodities has been expanding.

In the polycarbonate resin composition containing the PC-POS copolymer, investigations have been made on further improvements in impact resistance and flame retardancy thereof, and the impartment of any other characteristic, such as fluidity, thereto. For example, in each of Patent Documents 1 and 2, there is a disclosure of a thermoplastic resin that contains a predetermined amount of each of a polycarbonate resin, an acrylonitrile-styrene copolymer (hereinafter sometimes referred to as “AS”) or an acrylonitrile-butadiene-styrene copolymer (hereinafter sometimes referred to as “ABS”), a polysiloxane-polycarbonate copolymer, and a phosphorus-containing flame retardant, and that is improved in fluidity and flame retardancy substantially without the deterioration of its impact strength.

In each of Patent Documents 3 and 4, as a polycarbonate resin composition that satisfies moldability, impact resistance, and rigidity while maintaining excellent flame retardancy, and that can be molded into a molded body excellent in thermal stability, there is a disclosure of a polycarbonate resin composition containing, for example, a polycarbonate resin, a styrene-based resin, and a polycarbonate-polyorganosiloxane copolymer and/or a functional group-containing silicone compound.

CITATION LIST Patent Document

-   Patent Document 1: JP 2006-52401 A -   Patent Document 2: JP 2008-516013 A -   Patent Document 3: JP 2000-191898 A -   Patent Document 4: JP 2001-55500 A

SUMMARY OF INVENTION Technical Problem

A polycarbonate resin composition that can be molded into a thin-walled and large-sized molded body is required to have high fluidity comparable to that of an ABS resin. However, when an attempt is made to improve the fluidity of a polycarbonate resin composition containing a PC-POS copolymer, its impact strength tends to reduce, and hence it has heretofore been difficult to achieve both the fluidity and the impact strength at high levels.

An object of the present invention is to provide a polycarbonate-based resin composition that is excellent in fluidity, and can provide a molded body having a high impact strength.

Solution to Problem

The inventors of the present invention have found that the addition of a styrene-based resin to a polycarbonate-based resin composition including a polycarbonate-polyorganosiloxane copolymer and having a specific domain structure provides a polycarbonate-based resin composition that has more excellent impact resistance and is excellent in fluidity without the extension of the chain length of a polyorganosiloxane block or an increase in content thereof.

That is, the present invention relates to the following items [1] to [24].

[1] A polycarbonate-based resin composition, comprising:

a polycarbonate-based resin (S) satisfying the following requirements (1) and (2); and

a styrene-based resin (C) to be blended into the polycarbonate-based resin (S),

wherein a ratio of the polycarbonate-based resin (S) in 100 mass % of a total amount of the polycarbonate-based resin (S) and the styrene-based resin (C) is from 50 mass % or more to 99 mass % or less:

(1) the polycarbonate-based resin (S) contains a polycarbonate-polyorganosiloxane copolymer (A) containing a polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II), and an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and (2) the polycarbonate-based resin (S) has a structure in which a domain (d-1) containing the polyorganosiloxane block (A-2) is present in a matrix containing the aromatic polycarbonate-based resin (B) as a main component, and a domain (d-2) containing at least one selected from a block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d-1):

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4.

[2] A polycarbonate-based resin composition, comprising:

50 mass % or more to 99 mass % or less of a polycarbonate-based resin (S) containing a polycarbonate-polyorganosiloxane copolymer (A) containing a polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II), and an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and

1 mass % or more to 50 mass % or less of a styrene-based resin (C),

wherein the polycarbonate-based resin composition has a structure in which a domain (d^(C)-1) containing the polyorganosiloxane block (A-2) is present in a matrix containing the aromatic polycarbonate-based resin (B) as a main component, and a domain (d^(C)-2) containing at least one selected from a block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d^(C)-1), and

wherein a ratio of a number of domains (d^(C)) in each of which the domain (d^(C)-2) is present inside the domain (d^(C)-1) to a total number of the domains (d^(C)) and domains (d′^(C)) each formed only of the domain (d^(C)-1) is from 2% or more to 100% or less:

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4.

[3] The polycarbonate-based resin composition according to the above-mentioned item [1] or [2], wherein a mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) in the polycarbonate-based resin (S) is from 0.1/99.9 to 99.9/0.1.

[4] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [3], wherein the aromatic polycarbonate-based resin (B) contains a polycarbonate block including, in a main chain thereof, a repeating unit represented by the following general formula (III):

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to 4.

[5] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [4], wherein the domain (d-1) or (d^(C)-1) is mainly formed of the polyorganosiloxane block (A-2).

[6] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [5], wherein the domain (d-2) or (d^(C)-2) is mainly formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1).

[7] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [6], wherein only the one domain (d-2) is present inside the domain (d-1), or only the one domain (d^(C)-2) is present inside the domain (d^(C)-1).

[8] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [6], wherein the two or more domains (d-2) are present inside the domain (d-1), or the two or more domains (d^(C)-2) are present inside the domain (d^(C)-1).

[9] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] and [3] to [8], wherein a ratio of a number of domains (d) in each of which the domain (d-2) is present inside the domain (d-1) to a total number of the domains (d) and domains (d′) each formed only of the domain (d-1) is from 2% or more to 100% or less.

[10] The polycarbonate-based resin composition according to the above-mentioned item [9], wherein all domains corresponding to a total of the domains (d) and the domains (d′) or a total of the domains (d^(C)) and the domains (d′^(C)) have an average sectional area of 200 nm² or more.

[11] The polycarbonate-based resin composition according to the above-mentioned item [9] or [10], wherein all domains corresponding to a total of the domains (d) and the domains (d′) or a total of the domains (d^(C)) and the domains (d′^(C)) have an average sectional area of 20,000 nm² or less.

[12] The polycarbonate-based resin composition according to any one of the above-mentioned items [9] to [11], wherein an average of distances between adjacent particles of all domains corresponding to a total of the domains (d) and the domains (d′) or a total of the domains (d^(C)) and the domains (d′^(C)) is 500 nm or less.

[13] The polycarbonate-based resin composition according to any one of the above-mentioned items [9] to [12], wherein an average of distances between adjacent particles of all domains corresponding to a total of the domains (d) and the domains (d′) or a total of the domains (d^(C)) and the domains (d′^(C)) is 50 nm or more.

[14] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [13], wherein the polyorganosiloxane block (A-2) has an average chain length of from 30 or more to 500 or less.

[15] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [14], wherein the polyorganosiloxane block (A-2) has an average chain length of from 55 or more to 500 or less.

[16] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [15], wherein a content of the polyorganosiloxane block (A-2) in the polycarbonate-polyorganosiloxane copolymer (A) is from 10 mass % or more to 70 mass % or less.

[17] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [16], wherein a content of the polyorganosiloxane block (A-2) in the polycarbonate-based resin (S) is from 0.1 mass % or more to 10 mass % or less.

[18] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [17], wherein the polycarbonate-polyorganosiloxane copolymer (A) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.

[19] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [18], wherein the polycarbonate-based resin (S) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.

[20] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [19], wherein the styrene-based resin (C) has constituent units derived from acrylonitrile and styrene.

[21] The polycarbonate-based resin composition according to any one of the above-mentioned items [1] to [20], wherein the styrene-based resin (C) comprises at least one selected from an acrylonitrile-butadiene-styrene copolymer and an acrylonitrile-styrene copolymer.

[22] A molded article, which is obtained by molding the polycarbonate-based resin composition of any one of the above-mentioned items [1] to [21].

[23] The molded article according to the above-mentioned item [22], wherein the molded article comprises a casing for electrical and electronic equipment.

[24] The molded article according to the above-mentioned item [22], wherein the molded article comprises parts for an automobile and a building material.

Advantageous Effects of Invention

According to the present invention, the polycarbonate-based resin composition that has more excellent impact resistance and is excellent in fluidity, and the molded article of the composition can be obtained without the extension of the chain length of the polyorganosiloxane block or an increase in content thereof.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a view for illustrating the long-axis distance of a domain having one opening portion and the distance thereof between two contact points at the time of the drawing of a tangent of the domain, the tangent having two end portions of the opening portion as the contact points.

FIG. 2 is a view for illustrating the long-axis distance of a domain having two opening portions and each distance thereof between two contact points at the time of the drawing of a tangent of the domain, the tangent having two end portions of any one of the opening portions as the contact points.

FIG. 3 is a scanning probe microscope image for showing the long-axis distance of a domain having one opening portion and the distance thereof between two contact points at the time of the drawing of a tangent of the domain, the tangent having two end portions of the opening portion as the contact points.

FIG. 4 is a view for illustrating the position at which a test piece to be subjected to the observation of a domain structure with a SPM is cut out of an Izod test piece.

FIG. 5 is a view for illustrating a surface shaping adjustment procedure for a cut-out Izod sample piece for SPM observation.

FIG. 6 is a view for illustrating the shape of a glass knife used at the time of cutting with a microtome.

FIG. 7 is a photograph for showing a method of selecting a site to be observed with the SPM at a low magnification (10 microns by 10 microns).

FIG. 8 are an image of a domain structure observed with the SPM in Example 6 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 9 are an image of a domain structure observed with the SPM in Example 2 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 10 are an image of a domain structure observed with the SPM in Example 11 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 11 are an image of a domain structure observed with the SPM in Example 13 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 12 are an image of a domain structure observed with the SPM in Example 9 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 13 are an image of a domain structure observed with the SPM in Example 7 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 14 are an image of a domain structure observed with the SPM in Example 4 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 15 is an image of a domain structure observed with the SPM in Comparative Example 8.

FIG. 16 is an image of a domain structure observed with the SPM in Comparative Example 6.

FIG. 17 is an image of a domain structure observed with the SPM in Comparative Example 3.

FIG. 18 is a photograph for showing a method of selecting a site to be observed with the SPM at a low magnification (10 microns by 10 microns).

FIG. 19 are an image of a domain structure observed with the SPM in Example 25 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 20 are an image of a domain structure observed with the SPM in Example 20 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 21 are an image of a domain structure observed with the SPM in Example 26 and an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of the observed image.

FIG. 22 is an analyzed image in which a site recognized as a domain is painted in black at the time of the analysis of an image of a domain structure observed with the SPM in Reference Example 1.

DESCRIPTION OF EMBODIMENTS

The inventors of the present invention have made extensive investigations, and as a result, have found that the addition of a styrene-based resin to a polycarbonate-based resin including a polycarbonate-polyorganosiloxane copolymer and having a specific domain structure provides a polycarbonate-based resin composition that has more excellent impact resistance and is excellent in fluidity without any change in chain length or content of a polyorganosiloxane block. Detailed description is given below.

The term “XX to YY” as used herein means “from XX or more to YY or less.” In this description, a specification considered to be preferred may be arbitrarily adopted, and a combination of preferred specifications is more preferred.

<Polycarbonate-Based Resin Composition>

A polycarbonate-based resin composition according to a first embodiment of the present invention comprises:

a polycarbonate-based resin (S) satisfying the following requirements (1) and (2); and

a styrene-based resin (C) to be blended into the polycarbonate-based resin (S),

wherein a ratio of the polycarbonate-based resin (S) in 100 mass % of a total amount of the polycarbonate-based resin (S) and the styrene-based resin (C) is from 50 mass % or more to 99 mass % or less:

(1) the polycarbonate-based resin (S) contains a polycarbonate-polyorganosiloxane copolymer (A) containing a polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II), and an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and (2) the polycarbonate-based resin (S) has a structure in which a domain (d-1) containing the polyorganosiloxane block (A-2) is present in a matrix containing the aromatic polycarbonate-based resin (B) as a main component, and a domain (d-2) containing at least one selected from a block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d-1):

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “a” and “b” each independently represent an integer of from 0 to 4.

In the general formula (II), R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms.

Specific examples of R¹ to R⁴, X, “a”, and “b” in the formulae are described later.

The content of the polycarbonate-polyorganosiloxane copolymer (A) in the polycarbonate-based resin (S) is typically 0.1 mass % or more, preferably 1 mass % or more, more preferably 3 mass % or more, still more preferably 5 mass % or more, and is typically 99.9 mass % or less, preferably 99 mass % or less, more preferably 30 mass % or less, still more preferably 25 mass % or less, particularly preferably 17 mass % or less, most preferably 13 mass % or less from the viewpoint that a resin composition having desired properties, such as impact resistance, is obtained.

The content of the aromatic polycarbonate-based resin (B) in the polycarbonate-based resin (S) is typically 0.1 mass % or more, preferably 1 mass % or more, more preferably 50 mass % or more, still more preferably 70 mass % or more, still further more preferably 80 mass % or more, and is typically 99.9 mass % or less, preferably 99 mass % or less, more preferably 95 mass % or less, still more preferably 90 mass % or less from the viewpoint that a resin composition having desired properties, such as impact resistance, is obtained.

In one aspect of this embodiment, the total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) each forming the polycarbonate-based resin (S) is 100 mass %.

In the present invention, the mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) is typically from 0.1/99.9 to 99.9/0.1, preferably from 1/99 to 99/1, more preferably from 2/98 to 50/50, still more preferably from 5/95 to 20/80 from the viewpoint that a resin composition having desired properties, such as impact resistance, is obtained.

In the polycarbonate-based resin (S), the domain (d-1) containing the polyorganosiloxane block (A-2) is present in at least the matrix containing the aromatic polycarbonate-based resin (B) component as a main component, and the domain (d-2) containing at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is further present inside the domain (d-1). Only the one domain (d-2) may be present inside the one domain (d-1), or the two or more domains (d-2) may be present inside the one domain (d-1). Thus, the polycarbonate-based resin (S) necessarily has a domain (d) in which the at least one domain (d-2) is present inside the domain (d-1).

The matrix in the polycarbonate-based resin (S) is mainly formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) as long as the ratio of the polyorganosiloxane block (A-2) to the total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is not more than 50 mass %.

The domain (d-1) containing the polyorganosiloxane block (A-2) is preferably mainly formed of the polyorganosiloxane block (A-2).

The domain (d-2) containing at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is preferably mainly formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1), and may be mainly formed of any one of the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1), or may be mainly formed of both the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1).

Which block a detected domain is mainly formed of is judged from the contrast of an image obtained by observation with a scanning probe microscope (SPM). A domain showing contrast comparable to that of the matrix among the detected domains is judged to be mainly formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1). Similarly, a domain showing so dark contrast as to be clearly distinguished from the matrix among the detected domains is judged to be mainly formed of the polyorganosiloxane block (A-2).

In this embodiment, the domain (d-1) containing the polyorganosiloxane block (A-2) is substantially formed of the polyorganosiloxane block (A-2). The domain (d-2) containing at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is substantially formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1), and may be substantially formed of any one of the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1), or may be substantially formed of both the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1).

An example of the structure of the polycarbonate-based resin (S) in the polycarbonate-based resin composition of the invention of the present application is described in more detail. The polycarbonate-based resin (S) has a core-shell structure having the domain (d-1) forming a shell in the matrix and the one domain (d-2) forming a core therein. In addition, the resin may have a structure in which the two or more domains (d-2) each having a spherical shape or a cylindrical shape are incorporated inside the one domain (d-1), or a microphase-separated structure, such as a gyroid structure, a lamellar structure, or a salami structure.

When a domain different from the domain (d), the domain being formed only of the domain (d-1) containing the polyorganosiloxane block (A-2) (i.e., the (d-2) is not incorporated inside the (d-1)), is represented by (d′), the ratio of the number of the domains (d) to the total number of the domains (d) and the domains (d′) is preferably from 2% or more to 100% or less. When the ratio of the number of the domains (d) falls within the range, more excellent impact resistance can be obtained. The ratio of the number of the domains (d) is more preferably 5% or more, still more preferably 10% or more, still furthermore preferably 15% or more, still further more preferably 30% or more, particularly preferably 50% or more, and is more preferably 50% or less, still more preferably 45% or less, particularly preferably 30% or less. The numbers of the respective domains (d) and (d′) were visually measured with a SPM.

The average sectional area of all domains corresponding to the total of the domains (d) and the domains (d′) is preferably 200 nm² or more. When the average sectional area of all the domains is 200 nm² or more, more excellent impact resistance can be obtained. In addition, the average sectional area of all the domains corresponding to the total of the domains (d) and the domains (d′) is preferably 20,000 nm² or less. When the average sectional area of all the domains is 20,000 nm² or less, more excellent impact resistance can be obtained. The average sectional area of all the domains corresponding to the total of the domains (d) and the domains (d′) is more preferably 300 nm² or more, still more preferably 500 nm² or more, particularly preferably 1,000 nm² or more, and is more preferably 6,000 nm² or less, still more preferably 5,000 nm² or less, still further more preferably 4,000 nm² or less.

The average sectional area of the respective domains (d) and (d′) was calculated by observing the domains with a SPM and processing the resultant image with image analysis software (SPIP). Here, an average sectional area in the case where the domains (d) and (d′) each had an opening portion at the time of the observation with the SPM was calculated as described below. In the case where one domain had one opening portion as illustrated in FIG. 1, when a distance between two contact points at the time of the drawing of a tangent of the domain, the tangent having two end portions of the opening portion as the contact points, was ½ or less of the long-axis distance of the domain, the average sectional area was calculated as the average sectional area of the respective domains (d) and domains (d′) while the sectional area of the one domain was regarded as the sectional area of a domain free of the opening portion. In addition, in the case where one domain had two or more opening portions (two opening portions in FIG. 2) as illustrated in FIG. 2, when a distance between two contact points of each of the opening portions at the time of the drawing of a tangent of the domain, the tangent having two end portions of the opening portion as the contact points, was ½ or less of the long-axis distance of the domain, the sectional area of the one domain was regarded as the sectional area of a domain free of the respective opening portions. A scanning probe microscope image of a domain having one opening portion is shown in FIG. 3.

The average of distances between the adjacent particles of all the domains corresponding to the total of the domains (d) and the domains (d′) in the polycarbonate-based resin (S) is preferably 500 nm or less. When the average of the distances between the adjacent particles of all the domains is 500 nm or less, more excellent impact resistance can be obtained. In addition, the average of the distances between the adjacent particles of all the domains is preferably 50 nm or more. When the average of the distances between the adjacent particles of all the domains is 50 nm or more, more excellent impact resistance can be obtained.

The average of the distances between the adjacent particles of all the domains is more preferably 70 nm or more, still more preferably 110 nm or more, still further more preferably 130 nm or more, particularly preferably 180 nm or more, and is more preferably 350 nm or less, still more preferably 300 nm or less, particularly preferably 200 nm or less. The average of the distances between the adjacent particles of all the domains represents the frequency of presence of all the domains in the matrix. The average of the distances between the adjacent particles of all the domains was calculated by observing the particles with a SPM and processing the resultant image with image analysis software (SPIP).

Detailed conditions for the observation with the scanning probe microscope used in the measurement of the ratio of the number of the domains (d) to the total number of the domains (d) and the domains (d′), the average sectional area of all the domains, and the average of the distances between the adjacent particles of all the domains are described in Examples.

Although a cause for the result that the impact resistance of the polycarbonate-based resin composition of the present invention including the polycarbonate-based resin (S) becomes more excellent without the extension of the chain length of the polyorganosiloxane block or an increase in content thereof is unclear, the following is assumed to be responsible for the result.

That is, in the domain (d) of the polycarbonate-based resin composition according to the present invention, the domain (d-2) containing at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d-1) containing the polyorganosiloxane block (A-2).

When the amount of the polyorganosiloxane block (A-2) in the polycarbonate-based resin composition is the same as that of the foregoing composition, the domain (d) including the domain (d-2) is increased in size as compared to the domain (d′) formed only of the domain (d-1), and hence its size becomes larger than the size of the domain (d′). The size of the domain (d) present in the matrix entirely increases, and hence the propagation of a stress wave at the time of the application of an impact load to the polycarbonate-based resin composition may be further suppressed.

The content of the polyorganosiloxane block (A-2) in the polycarbonate-based resin (S) is preferably 0.1 mass % or more, more preferably 0.4 mass % or more, still more preferably 0.8 mass % or more, still further more preferably 1 mass % or more, particularly preferably 3 mass % or more, and is preferably 10 mass % or less, more preferably 7.0 mass % or less, still more preferably 6 mass % or less, particularly preferably 5 mass % or less, most preferably 4 mass % or less. When the content of the polyorganosiloxane block (A-2) in the polycarbonate-based resin (S) falls within the range, an excellent impact-resisting characteristic can be obtained.

The viscosity-average molecular weight (Mv) of the polycarbonate-based resin (S) may be appropriately adjusted by using, for example, a molecular weight modifier (terminal stopper) so as to be a target molecular weight in accordance with applications or products in which the polycarbonate-based resin is used. The viscosity-average molecular weight of the polycarbonate-based resin (S) is preferably 9,000 or more, more preferably 12,000 or more, still more preferably 14,000 or more, particularly preferably 16,000 or more, and is preferably 50,000 or less, more preferably 30,000 or less, still more preferably 23,000 or less, particularly preferably 22,000 or less. When the viscosity-average molecular weight is 9,000 or more, a sufficient strength of a molded article can be obtained. When the viscosity-average molecular weight is 50,000 or less, injection molding or extrusion molding can be performed at the temperature at which the heat deterioration of the polycarbonate-based resin does not occur.

The viscosity-average molecular weight (Mv) is a value calculated from the following Schnell's equation by measuring the limiting viscosity [η] of a methylene chloride solution at 20° C. [η]=1.23×10⁻⁵×Mv^(0.83)

A polycarbonate-based resin composition according to a second embodiment of the present invention comprises:

50 mass % or more to 99 mass % or less of a polycarbonate-based resin (S) containing a polycarbonate-polyorganosiloxane copolymer (A) containing a polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II), and an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and

1 mass % or more to 50 mass % or less of a styrene-based resin (C),

wherein the polycarbonate-based resin composition has a structure in which a domain (d^(C)-1) containing the polyorganosiloxane block (A-2) is present in a matrix containing the aromatic polycarbonate-based resin (B) as a main component, and a domain (d^(C)-2) containing at least one selected from a block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d^(C)-1), and

wherein a ratio of a number of domains (d^(C)) in each of which the domain (d^(C)-2) is present inside the domain (d^(C)-1) to a total number of the domains (d^(C)) and domains (d′^(C)) each formed only of the domain (d^(C)-1) is from 2% or more to 100% or less:

wherein R¹, R², X, R³, R⁴, “a”, and “b” are as described above.

The polycarbonate-based resin composition according to the second embodiment of the present invention has the same domain structure as that of the polycarbonate-based resin (S) described in the above-mentioned first embodiment. Which block a detected domain is mainly formed of is judged from the contrast of an image obtained by observation with a scanning probe microscope as in the polycarbonate-based resin (S).

That is, as in the first embodiment, the domain (d^(C)-1) corresponding to the domain (d-1) is present in the matrix containing the aromatic polycarbonate-based resin (B) component as a main component, and the domain (d^(C)-2) corresponding to the domain (d-2) is present inside the domain (d^(C)-1). Only the one domain (d^(C)-2) may be present inside the one domain (d^(C)-1), or the two or more domains (d^(C)-2) may be present inside the one domain (d^(C)-1). Thus, the polycarbonate-based resin composition necessarily has the domain (d^(C)) in which the at least one domain (d^(C)-2) is present inside the domain (d^(C)-1)

In the same manner as described above, the matrix in the polycarbonate-based resin composition is mainly formed of at least one selected from the block derived from the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) as long as the ratio of the polyorganosiloxane block (A-2) to the total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) serving as resin components is not more than 50 mass %.

Resin components forming the domain (d^(C)-1) and the domain (d^(C)-2) are the same as those of the domain (d-1) and the domain (d-2). In addition, as in the polycarbonate-based resin (S), the polycarbonate-based resin composition has a core-shell structure having the domain (d^(C)-1) forming a shell in the matrix and the one domain (d^(C)-2) forming a core therein. In addition, the composition may have a structure in which the two or more domains (d^(C)-2) each having a spherical shape or a cylindrical shape are incorporated inside the one domain (d^(C)-1), or a microphase-separated structure, such as a gyroid structure, a lamellar structure, or a salami structure.

In the second embodiment, when a domain free of the domain (d^(C)-2) inside the domain (d^(C)-1) (i.e., corresponding to the domain (d′) in the first embodiment) is represented by (d′^(C)), the ratio of the number of the domains (d^(C)) to the total number of the domains (d^(C)) and the domains (d′^(C)) needs to be from 2% or more to 100% or less. When the ratio of the number of the domains (d^(C)) falls within the range, more excellent impact resistance can be obtained. The ratio of the number of the domains (d^(C)) is more preferably 5% or more, still more preferably 15% or more, still further more preferably 30% or more, still further more preferably 50% or more, particularly preferably 60% or more, and is more preferably 90% or less, still more preferably 80% or less, still further more preferably 75% or less, still further more preferably 50% or less, still further more preferably 45% or less, particularly preferably 30% or less. The numbers of the respective domains (d^(C)) and (d′^(C)) were visually measured with a SPM.

The average sectional area of all domains corresponding to the total of the domains (d^(C)) and the domains (d′^(C)) is preferably 200 nm² or more. When the average sectional area of all the domains is 200 nm² or more, more excellent impact resistance can be obtained. In addition, the average sectional area of all the domains corresponding to the total of the domains (d^(C)) and the domains (d′^(C)) is preferably 20,000 nm² or less. When the average sectional area of all the domains is 20,000 nm² or less, more excellent impact resistance can be obtained. The average sectional area of all the domains corresponding to the total of the domains (d^(C)) and the domains (d′^(C)) is more preferably 300 nm² or more, still more preferably 500 nm² or more, particularly preferably 1,000 nm² or more, and is more preferably 6,000 nm² or less, still more preferably 5,000 nm² or less, still further more preferably 4,000 nm² or less.

As in the first embodiment, the average sectional area of the respective domains (d^(C)) and (d′^(C)) was calculated by observing the domains with a SPM and processing the resultant image with image analysis software (SPIP). A method of calculating the average sectional area and a method of judging the presence or absence of an opening portion are as described in the first embodiment.

The average of distances between the adjacent particles of all the domains corresponding to the total of the domains (d^(C)) and the domains (d′^(C)) in the polycarbonate-based resin composition is preferably 500 nm or less. When the average of the distances between the adjacent particles of all the domains is 500 nm or less, more excellent impact resistance can be obtained. In addition, the average of the distances between the adjacent particles of all the domains is preferably 50 nm or more. When the average of the distances between the adjacent particles of all the domains is 50 nm or more, more excellent impact resistance can be obtained.

The average of the distances between the adjacent particles of all the domains is more preferably 70 nm or more, still more preferably 110 nm or more, still further more preferably 130 nm or more, particularly preferably 180 nm or more, and is more preferably 350 nm or less, still more preferably 300 nm or less, particularly preferably 200 nm or less. As in the first embodiment, the average of the distances between the adjacent particles of all the domains represents the frequency of presence of all the domains in the matrix. The average of the distances between the adjacent particles of all the domains was calculated by observing the particles with a SPM and processing the resultant image with image analysis software (SPIP).

Detailed conditions for the observation with the scanning probe microscope used in the measurement of the ratio of the number of the domains (d^(C)) to the total number of the domains (d^(C)) and the domains (d′^(C)), the average sectional area of all the domains, and the average of the distances between the adjacent particles of all the domains are described in Examples.

<Polycarbonate-Polyorganosiloxane Copolymer (A)>

The respective components in the first embodiment and the second embodiment are described in more detail below.

As described above, the domain (d-1) contains the following polyorganosiloxane block (A-2) of the polycarbonate-polyorganosiloxane copolymer (A), and is preferably mainly formed of the polyorganosiloxane block (A-2). As described above, the polycarbonate-polyorganosiloxane copolymer (A) contains the polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and the polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II):

wherein in the general formulae (I) and (II), R¹ to R⁴, X, “a”, and “b” are as described above.

In the general formula (I), examples of the halogen atom that R¹ and R² each independently represent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

Examples of the alkyl group that R¹ and R² each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups (the term “various” means that a linear group and all kinds of branched groups are included, and in this description, the same holds true for the following), various pentyl groups, and various hexyl groups. Examples of the alkoxy group that R¹ and R² each independently represent include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties.

Examples of the alkylene group represented by X include a methylene group, an ethylene group, a trimethylene group, a tetramethylene group, and a hexamethylene group. Among them, an alkylene group having 1 to 5 carbon atoms is preferred. Examples of the alkylidene group represented by X include an ethylidene group and an isopropylidene group. Examples of the cycloalkylene group represented by X include a cyclopentanediyl group, a cyclohexanediyl group, and a cyclooctanediyl group. Among them, a cycloalkylene group having 5 to 10 carbon atoms is preferred. Examples of the cycloalkylidene group represented by X include a cyclohexylidene group, a 3,5,5-trimethylcyclohexylidene group, and a 2-adamantylidene group. Among them, a cycloalkylidene group having 5 to 10 carbon atoms is preferred, and a cycloalkylidene group having 5 to 8 carbon atoms is more preferred. Examples of the aryl moiety of the arylalkylene group represented by X include aryl groups each having 6 to 14 ring-forming carbon atoms, such as a phenyl group, a naphthyl group, a biphenyl group, and an anthryl group, and examples of the alkylene group include the above-mentioned alkylene groups. Examples of the aryl moiety of the arylalkylidene group represented by X include aryl groups each having 6 to 14 ring-forming carbon atoms, such as a phenyl group, a naphthyl group, a biphenyl group, and an anthryl group, and examples of the alkylidene group may include the above-mentioned alkylidene groups.

“a” and “b” each independently represent an integer of from 0 to 4, preferably from 0 to 2, more preferably 0 or 1.

Among them, a repeating unit in which “a” and “b” each represent 0, and X represents a single bond or an alkylene group having 1 to 8 carbon atoms, or a repeating unit in which “a” and “b” each represent 0, and X represents an alkylene group having 3 carbon atoms, in particular an isopropylidene group is suitable.

In the general formula (II), examples of the halogen atom represented by R³ or R⁴ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Examples of the alkyl group represented by R³ or R⁴ include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the alkoxy group represented by R³ or R⁴ include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties. Examples of the aryl group represented by R³ or R⁴ include a phenyl group and a naphthyl group.

R³ and R⁴ each preferably represent a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and each more preferably represent a methyl group.

More specifically, the polyorganosiloxane block (A-2) containing the repeating unit represented by the general formula (II) preferably has a unit represented by any one of the following general formulae (II-I) to (II-III):

wherein R³ to R⁶ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and a plurality of R³, R⁴, R⁵, or R⁶ may be identical to or different from each other, Y represents —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —COO—, —S—, —R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O—, and a plurality of Ys may be identical to or different from each other, the R⁷ represents a single bond, a linear, branched, or cyclic alkylene group, an aryl-substituted alkylene group, a substituted or unsubstituted arylene group, or a diarylene group, R⁸ represents an alkyl group, an alkenyl group, an aryl group, or an aralkyl group, R⁹ represents a diarylene group, R¹⁰ represents a linear, branched, or cyclic alkylene group, or a diarylene group, β represents a divalent group derived from a diisocyanate compound, or a divalent group derived from a dicarboxylic acid or a halide of a dicarboxylic acid, “n” represents the chain length of the polyorganosiloxane, and n−1, and “p” and “q” each represent the number of repetitions of a polyorganosiloxane unit and each represent an integer of 1 or more, and the sum of “p” and “q” is n−2.

Examples of the halogen atom that R³ to R⁶ each independently represent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Examples of the alkyl group that R³ to R⁶ each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the alkoxy group that R³ to R⁶ each independently represent include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties. Examples of the aryl group that R³ to R⁶ each independently represent include a phenyl group and a naphthyl group.

R³ to R⁶ each preferably represent a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms.

R³ to R⁶ in the general formula (II-I), the general formula (II-II), and/or the general formula (II-III) each preferably represent a methyl group.

The linear or branched alkylene group represented by R⁷ in —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O— represented by Y is, for example, an alkylene group having 1 to 8 carbon atoms, preferably 1 to 5 carbon atoms, and the cyclic alkylene group represented by R⁷ is, for example, a cycloalkylene group having 5 to 15 carbon atoms, preferably 5 to 10 carbon atoms.

The aryl-substituted alkylene group represented by R⁷ may have a substituent, such as an alkoxy group or an alkyl group, on its aromatic ring, and a specific structure thereof may be, for example, a structure represented by the following general formula (i) or (ii). When the block has the aryl-substituted alkylene group, the alkylene group is bonded to Si.

wherein “c” represents a positive integer and typically represents an integer of from 1 to 6.

The diarylene group represented by any one of R⁷, R⁹, and R¹⁰ refers to a group in which two arylene groups are linked to each other directly or through a divalent organic group, and is specifically a group having a structure represented by —Ar¹—W—Ar²—. Here, Ar¹ and Ar² each represent an arylene group, and W represents a single bond or a divalent organic group. Examples of the divalent organic group represented by W include an isopropylidene group, a methylene group, a dimethylene group, and a trimethylene group.

Examples of the arylene group represented by any one of R⁷, Ar¹, and Ar² include arylene groups each having 6 to 14 ring-forming carbon atoms, such as a phenylene group, a naphthylene group, a biphenylene group, and an anthrylene group. Those arylene groups may each have an arbitrary substituent, such as an alkoxy group or an alkyl group.

The alkyl group represented by R⁸ is a linear or branched group having 1 to 8, preferably 1 to 5 carbon atoms. The alkenyl group represented by R⁸ is, for example, a linear or branched group having 2 to 8, preferably 2 to 5 carbon atoms. The aryl group represented by R⁸ is, for example, a phenyl group or a naphthyl group. The aralkyl group represented by R⁸ is, for example, a phenylmethyl group or a phenylethyl group.

The linear, branched, or cyclic alkylene group represented by R¹⁰ is the same as that represented by R⁷.

Y preferably represents —R⁷O—. R⁷ preferably represents an aryl-substituted alkylene group, in particular a residue of a phenol-based compound having an alkyl group, and more preferably represents an organic residue derived from allylphenol or an organic residue derived from eugenol.

With regard to “p” and “q” in the formula (II-II), it is preferred that p=q.

In addition, β represents a divalent group derived from a diisocyanate compound, or a divalent group derived from a dicarboxylic acid or a halide of a dicarboxylic acid, and examples thereof include divalent groups represented by the following general formulae (iii) to (vii).

The average chain length “n” of the polyorganosiloxane block (A-2) in the PC-POS copolymer (A) is preferably 30 or more, more preferably 35 or more, still more preferably 40 or more, still further more preferably 50 or more, particularly preferably 55 or more, most preferably 60 or more. In addition, the average chain length is preferably 500 or less, more preferably 400 or less, still more preferably 300 or less, still further more preferably 200 or less, particularly preferably 120 or less, most preferably 85 or less. The average chain length is calculated by nuclear magnetic resonance (NMR) measurement. When the average chain length “n” falls within the range of from 30 or more to 500 or less, more excellent impact resistance can be obtained. In addition, the average chain length “n” of the polyorganosiloxane block (A-2) preferably falls within the range of from 55 or more to 500 or less from the viewpoint that more excellent impact resistance is obtained.

The content of the polyorganosiloxane block (A-2) in the PC-POS copolymer (A) is preferably 5 mass % or more, more preferably 6 mass % or more, still more preferably 10 mass % or more, still further more preferably 14 mass % or more, still further more preferably 18 mass % or more, particularly preferably 21 mass % or more. In addition, the content is preferably 70 mass % or less, more preferably 50 mass % or less, still more preferably 45 mass % or less, particularly preferably 40 mass % or less. When the content of the polyorganosiloxane block in the PC-POS copolymer (A) falls within the range, more excellent impact resistance can be obtained.

The viscosity-average molecular weight (Mv) of the PC-POS copolymer (A) may be appropriately adjusted by using, for example, a molecular weight modifier (terminal stopper) so as to be a target molecular weight in accordance with applications or products in which the copolymer is used. However, the viscosity-average molecular weight is preferably 9,000 or more, more preferably 12,000 or more, still more preferably 14,000 or more, particularly preferably 16,000 or more, and is preferably 50,000 or less, more preferably 30,000 or less, still more preferably 23,000 or less, particularly preferably 22,000 or less, most preferably 20,000 or less. When the viscosity-average molecular weight is 9,000 or more, a sufficient strength of a molded article can be obtained. When the viscosity-average molecular weight is 50,000 or less, injection molding or extrusion molding can be performed at the temperature at which the heat deterioration of the copolymer does not occur.

The viscosity-average molecular weight (Mv) is a value calculated from the following Schnell's equation by measuring the limiting viscosity [η] of a methylene chloride solution at 20° C. [η]=1.23×10⁻⁵×Mv^(0.83)

The polycarbonate-polyorganosiloxane copolymer (A) may be produced by a known production method, such as an interfacial polymerization method (phosgene method), a pyridine method, or an ester exchange method. Particularly in the case of the interfacial polymerization method, a step of separating an organic phase containing the PC-POS copolymer (A) and an aqueous phase containing an unreacted product, a catalyst residue, or the like becomes easier, and hence the separation of the organic phase containing the PC-POS copolymer (A) and the aqueous phase in each washing step based on alkali washing, acid washing, or pure water washing becomes easier. Accordingly, the PC-POS copolymer (A) is efficiently obtained. With regard to a method of producing the PC-POS copolymer (A), reference may be made to, for example, a method described in JP 2010-241943 A.

Specifically, the PC-POS copolymer (A) may be produced by: dissolving a polycarbonate oligomer produced in advance to be described later and a polyorganosiloxane in a water-insoluble organic solvent (e.g., methylene chloride); adding a solution of a dihydric phenol-based compound (e.g., bisphenol A) in an aqueous alkali compound (e.g., aqueous sodium hydroxide) to the solution; and subjecting the mixture to an interfacial polycondensation reaction through the use of a tertiary amine (e.g., triethylamine) or a quaternary ammonium salt (e.g., trimethylbenzylammonium chloride) as a polymerization catalyst in the presence of a terminal stopper (a monohydric phenol, such as p-tert-butylphenol). In addition, the PC-POS copolymer (A) may also be produced by copolymerizing the polyorganosiloxane and a dihydric phenol, and phosgene, a carbonate ester, or a chloroformate.

When the polycarbonate-polyorganosiloxane copolymer (A) in the polycarbonate-based resin composition of the present application is produced by, for example, causing the polycarbonate oligomer and a polyorganosiloxane raw material to react with each other in an organic solvent, and then causing the resultant to react with the dihydric phenol, the solid content weight (g/L) of the polycarbonate oligomer in 1 L of a mixed solution of the organic solvent and the polycarbonate oligomer preferably falls within the range of from 80 g/L or more to 200 g/L or less. The solid content weight is more preferably 90 g/L or more, still more preferably 100 g/L or more, and is more preferably 180 g/L or less, still more preferably 170 g/L or less.

A polyorganosiloxane represented by the following general formula (1), general formula (2), and/or general formula (3) may be used as the polyorganosiloxane serving as a raw material:

wherein

R³ to R⁶, Y, β, n−1, “p”, and “q” are as described above, and specific examples and preferred examples thereof are also the same as those described above, and

Z represents a hydrogen atom or a halogen atom, and a plurality of Z may be identical to or different from each other.

Examples of the polyorganosiloxane represented by the general formula (1) include compounds each represented by any one of the following general formulae (1-1) to (1-11):

wherein in the general formulae (1-1) to (1-11), R³ to R⁶, “n”, and R⁸ are as defined above, and preferred examples thereof are also the same as those described above, and “c” represents a positive integer and typically represents an integer of from 1 to 6.

Among them, a phenol-modified polyorganosiloxane represented by the general formula (1-1) is preferred from the viewpoint of its ease of polymerization. In addition, an α,ω-bis [3-(o-hydroxyphenyl)propyl]polydimethylsiloxane, which is one compound represented by the general formula (1-2), or an α,ω-bis [3-(4-hydroxy-3-methoxyphenyl) propyl]polydimethylsiloxane, which is one compound represented by the general formula (1-3), is preferred from the viewpoint of its ease of availability.

In addition to the foregoing, a compound having a structure represented by the following general formula (4) may be used as a polyorganosiloxane raw material:

wherein R³ and R⁴ are identical to those described above. The average chain length of the polyorganosiloxane block represented by the general formula (4) is (r×m), and the range of the (r×m) is the same as that of the “n”.

When the compound represented by the general formula (4) is used as a polyorganosiloxane raw material, the polyorganosiloxane block (A-2) preferably has a unit represented by the following general formula (II-IV):

wherein R³, R⁴, “r”, and “m” are as described above.

The copolymer may include a structure represented by the following general formula (II-V) as the polyorganosiloxane block (A-2):

wherein R¹⁸ to R²¹ each independently represent a hydrogen atom or an alkyl group having 1 to 13 carbon atoms, R²² represents an alkyl group having 1 to 6 carbon atoms, a hydrogen atom, a halogen atom, a hydroxy group, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 14 carbon atoms, Q² represents a divalent aliphatic group having 1 to 10 carbon atoms, and “n” represents an average chain length and represents from 30 to 70.

In the general formula (II-V), examples of the alkyl group having 1 to 13 carbon atoms that R¹⁸ to R²¹ each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, various hexyl groups, various heptyl groups, various octyl groups, a 2-ethylhexyl group, various nonyl groups, various decyl groups, various undecyl groups, various dodecyl groups, and various tridecyl groups. Among them, R¹⁸ to R²¹ each preferably represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and it is more preferred that all of R¹⁸ to R²¹ each represent a methyl group.

Examples of the alkyl group having 1 to 6 carbon atoms represented by R²² include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the halogen atom represented by R²² include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. An example of the alkoxy group having 1 to 6 carbon atoms represented by R²² is an alkoxy group whose alkyl group moiety is the alkyl group described above. In addition, examples of the aryl group having 6 to 14 carbon atoms represented by R²² include a phenyl group, a toluyl group, a dimethylphenyl group, and a naphthyl group.

Among them, R²² preferably represents a hydrogen atom or an alkoxy group having 1 to 6 carbon atoms, more preferably represents a hydrogen atom or an alkoxy group having 1 to 3 carbon atoms, and still more preferably represents a hydrogen atom.

The divalent aliphatic group having 1 to 10 carbon atoms represented by Q² is preferably a linear or branched divalent saturated aliphatic group having 1 to 10 carbon atoms. The number of carbon atoms of the saturated aliphatic group is preferably from 1 to 8, more preferably from 2 to 6, still more preferably from 3 to 6, still further more preferably from 4 to 6. In addition, the average chain length “n” is as described above.

A preferred mode of the constituent unit (II-V) may be, for example, a structure represented by the following general formula (II-VI):

wherein “n” is identical to that described above.

The polyorganosiloxane block (A-2) represented by the general formula (II-V) or (II-VI) may be obtained by using a polyorganosiloxane raw material represented by the following general formula (5) or (6):

wherein R¹⁸ to R²², Q², and “n” are as described above;

wherein “n” is as described above.

A method of producing the polyorganosiloxane is not particularly limited. According to, for example, a method described in JP 11-217390 A, a crude polyorganosiloxane may be obtained by: causing cyclotrisiloxane and disiloxane to react with each other in the presence of an acid catalyst to synthesize α,ω-dihydrogen organopentasiloxane; and then subjecting the α,ω-dihydrogen organopentasiloxane to an addition reaction with, for example, a phenolic compound (e.g., 2-allylphenol, 4-allylphenol, eugenol, or 2-propenylphenol) in the presence of a catalyst for a hydrosilylation reaction. In addition, according to a method described in JP 2662310 B2, the crude polyorganosiloxane may be obtained by: causing octamethylcyclotetrasiloxane and tetramethyldisiloxane to react with each other in the presence of sulfuric acid (acid catalyst); and subjecting the resultant α,ω-dihydrogen organopolysiloxane to an addition reaction with the phenolic compound or the like in the presence of the catalyst for a hydrosilylation reaction in the same manner as that described above. The α,ω-dihydrogen organopolysiloxane may be used after its chain length “n” has been appropriately adjusted in accordance with its polymerization conditions, or a commercial α,ω-dihydrogen organopolysiloxane may be used.

Examples of the catalyst for a hydrosilylation reaction include transition metal-based catalysts. Among them, a platinum-based catalyst is preferably used in terms of a reaction rate and selectivity. Specific examples of the platinum-based catalyst include chloroplatinic acid, an alcohol solution of chloroplatinic acid, an olefin complex of platinum, a complex of platinum and a vinyl group-containing siloxane, platinum-supported silica, and platinum-supported activated carbon.

The crude polyorganosiloxane is preferably brought into contact with an adsorbent to cause the adsorbent to adsorb and remove a transition metal derived from a transition metal-based catalyst in the crude polyorganosiloxane, the catalyst having been used as the catalyst for a hydrosilylation reaction.

An adsorbent having an average pore diameter of, for example, 1,000 Å or less may be used as the adsorbent. When the average pore diameter is 1,000 Å or less, the transition metal in the crude polyorganosiloxane can be efficiently removed. From such viewpoint, the average pore diameter of the adsorbent is preferably 500 Å or less, more preferably 200 Å or less, still more preferably 150 Å or less, still further more preferably 100 Å or less. In addition, from the same viewpoint, the adsorbent is preferably a porous adsorbent.

Although the adsorbent is not particularly limited as long as the adsorbent has the above-mentioned average pore diameter, for example, activated clay, acid clay, activated carbon, synthetic zeolite, natural zeolite, activated alumina, silica, a silica-magnesia-based adsorbent, diatomaceous earth, or cellulose may be used, and at least one selected from the group consisting of activated clay, acid clay, activated carbon, synthetic zeolite, natural zeolite, activated alumina, silica, and a silica-magnesia-based adsorbent is preferred.

After the adsorbent has been caused to adsorb the transition metal in the crude polyorganosiloxane, the adsorbent may be separated from the polyorganosiloxane by arbitrary separating means. Examples of the means for separating the adsorbent from the polyorganosiloxane include a filter and centrifugal separation. When the filter is used, a filter such as a membrane filter, a sintered metal filter, or a glass fiber filter may be used. Among them, a membrane filter is particularly preferably used.

The average particle diameter of the adsorbent is typically from 1 μm or more to 4 mm or less, preferably from 1 μm or more to 100 μm or less from the viewpoint that the adsorbent is separated from the polyorganosiloxane after the adsorption of the transition metal.

When the adsorbent is used, its usage amount is not particularly limited. The porous adsorbent may be used in an amount in the range of preferably from 1 part by mass or more to 30 parts by mass or less, more preferably from 2 parts by mass or more to 20 parts by mass or less with respect to 100 parts by mass of the crude polyorganosiloxane.

When the crude polyorganosiloxane to be treated has so high a molecular weight that the polyorganosiloxane is not in a liquid state, the polyorganosiloxane may be heated to such a temperature as to be in a liquid state at the time of the performance of the adsorption with the adsorbent and the separation of the adsorbent. Alternatively, the adsorption and the separation may be performed after the polyorganosiloxane has been dissolved in a solvent, such as methylene chloride or hexane.

A polyorganosiloxane having a desired molecular weight distribution is obtained by regulating its molecular weight distribution through, for example, the blending of a plurality of polyorganosiloxanes. With regard to the blending, a crude polyorganosiloxane having a desired molecular weight distribution may be obtained by blending a plurality of α,ω-dihydrogen organopolysiloxanes and then subjecting a phenolic compound or the like to an addition reaction with the resultant in the presence of a catalyst for a hydrosilylation reaction. In addition, purification, such as the removal of the catalyst for a hydrosilylation reaction, may be performed after a plurality of crude polyorganosiloxanes have been blended. A plurality of polyorganosiloxanes after the purification may be blended. In addition, a molecular weight distribution may be appropriately adjusted depending on a polymerization condition at the time of the production of a polyorganosiloxane. In addition, a desired molecular weight distribution may be obtained by fractionating only part of existing polyorganosiloxanes through means such as various kinds of separation.

The polycarbonate oligomer may be produced by a reaction between a dihydric phenol and a carbonate precursor, such as phosgene or triphosgene, in an organic solvent, such as methylene chloride, chlorobenzene, or chloroform. When the polycarbonate oligomer is produced by using an ester exchange method, the oligomer may be produced by a reaction between the dihydric phenol and a carbonate precursor, such as diphenyl carbonate.

A dihydric phenol represented by the following general formula (viii) is preferably used as the dihydric phenol:

wherein R¹, R², “a”, “b”, and X are as described above.

Examples of the dihydric phenol represented by the general formula (viii) include: bis(hydroxyphenyl)alkane-based dihydric phenols, such as 2,2-bis(4-hydroxyphenyl)propane [bisphenol A], bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl) ethane, and 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane; 4,4′-dihydroxydiphenyl; bis(4-hydroxyphenyl)cycloalkanes; bis(4-hydroxyphenyl) oxide; bis(4-hydroxyphenyl) sulfide; bis(4-hydroxyphenyl) sulfone; bis(4-hydroxyphenyl) sulfoxide; and bis(4-hydroxyphenyl) ketone. Those dihydric phenols may be used alone or as a mixture thereof.

Among them, bis(hydroxyphenyl) alkane-based dihydric phenols are preferred, and bisphenol A is more preferred. When bisphenol A is used as the dihydric phenol, the PC-POS copolymer is such that in the general formula (i), X represents an isopropylidene group and a=b=0.

Examples of the dihydric phenol except bisphenol A include bis(hydroxyaryl)alkanes, bis(hydroxyaryl)cycloalkanes, dihydroxyaryl ethers, dihydroxydiaryl sulfides, dihydroxydiaryl sulfoxides, dihydroxydiaryl sulfones, dihydroxydiphenyls, dihydroxydiaryl fluorenes, and dihydroxydiaryl adamantanes. Those dihydric phenols may be used alone or as a mixture thereof.

Examples of the bis(hydroxyaryl)alkanes include bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane, bis(4-hydroxyphenyl)phenylmethane, bis(4-hydroxyphenyl)diphenylmethane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, bis(4-hydroxyphenyl)naphthylmethane, 1,1-bis(4-hydroxy-3-tert-butylphenyl)propane, 2,2-bis(4-hydroxy-3-bromophenyl)propane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, 2,2-bis(4-hydroxy-3-chlorophenyl)propane, 2,2-bis(4-hydroxy-3,5-dichlorophenyl)propane, and 2,2-bis(4-hydroxy-3,5-dibromophenyl)propane.

Examples of the bis(hydroxyaryl)cycloalkanes include 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 1,1-bis(4-hydroxyphenyl)-3,5,5-trimethylcyclohexane, 2,2-bis(4-hydroxyphenyl)norbornane, and 1,1-bis(4-hydroxyphenyl) cyclododecane. Examples of the dihydroxyaryl ethers include 4,4′-dihydroxydiphenyl ether and 4,4′-dihydroxy-3,3′-dimethylphenyl ether.

Examples of the dihydroxydiaryl sulfides include 4,4′-dihydroxydiphenyl sulfide and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide. Examples of the dihydroxydiaryl sulfoxides include 4,4′-dihydroxydiphenyl sulfoxide and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfoxide. Examples of the dihydroxydiaryl sulfones include 4,4′-dihydroxydiphenyl sulfone and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone.

An example of the dihydroxydiphenyls is 4,4′-dihydroxydiphenyl. Examples of the dihydroxydiaryl fluorenes include 9,9-bis(4-hydroxyphenyl)fluorene and 9,9-bis(4-hydroxy-3-methylphenyl) fluorene. Examples of the dihydroxydiaryladamantanes include 1,3-bis(4-hydroxyphenyl)adamantane, 2,2-bis(4-hydroxyphenyl)adamantane, and 1,3-bis(4-hydroxyphenyl)-5,7-dimethyladamantane.

Examples of dihydric phenols except those described above include 4,4′-[1,3-phenylenebis(1-methylethylidene)]bisphenol, 10,10-bis(4-hydroxyphenyl)-9-anthrone, and 1,5-bis(4-hydroxyphenylthio)-2,3-dioxapentane.

In order to adjust the molecular weight of the PC-POS copolymer to be obtained, a terminal stopper (molecular weight modifier) may be used. Examples of the terminal stopper may include monohydric phenols, such as phenol, p-cresol, p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol, p-nonylphenol, m-pentadecylphenol, and p-tert-amylphenol. Those monohydric phenols may be used alone or in combination thereof.

After the interfacial polycondensation reaction, the PC-POS copolymer (A) may be obtained by appropriately leaving the resultant at rest to separate the resultant into an aqueous phase and an organic solvent phase [separating step], washing the organic solvent phase (preferably washing the phase with a basic aqueous solution, an acidic aqueous solution, and water in the stated order) [washing step], concentrating the resultant organic phase [concentrating step], and drying the concentrated phase [drying step].

<(B) Aromatic Polycarbonate-Based Resin>

The aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A) forms the matrix portion of the polycarbonate-based resin (S) and may be contained in the domain (d-2).

The aromatic polycarbonate-based resin (B) includes, in a main chain thereof, a repeating unit represented by the following general formula (III). The polycarbonate-based resin is not particularly limited, and various known polycarbonate-based resins may each be used.

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to 4.

Specific examples of R³⁰ and R³¹ include the same examples as those of R¹ and R², and preferred examples thereof are also the same as those of R¹ and R². R³⁰ and R³¹ each more preferably represent an alkyl group having 1 to 6 carbon atoms or an alkoxy group having 1 to 6 carbon atoms. Specific examples of X′ include the same examples as those of X, and preferred examples thereof are also the same as those of X. “d” and “e” each independently represent preferably from 0 to 2, more preferably 0 or 1.

Specifically, a resin obtained by a conventional production method for a polycarbonate may be used as the aromatic polycarbonate-based resin (B). Examples of the conventional method include: an interfacial polymerization method involving causing the dihydric phenol-based compound and phosgene to react with each other in the presence of an organic solvent inert to the reaction and an aqueous alkali solution, adding a polymerization catalyst, such as a tertiary amine or a quaternary ammonium salt, to the resultant, and polymerizing the mixture; and a pyridine method involving dissolving the dihydric phenol-based compound in pyridine or a mixed solution of pyridine and an inert solvent, and introducing phosgene to the solution to directly produce the resin.

A molecular weight modifier (terminal stopper), a branching agent, or the like is used as required in the reaction.

The dihydric phenol-based compound is, for example, a compound represented by the following general formula (III′):

wherein R³⁰, R³¹, X′, “d”, and “e” are as defined above, and preferred examples thereof are also the same as those described above.

Specific examples of the dihydric phenol-based compound may include those described above in the method of producing the polycarbonate-polyorganosiloxane copolymer (A), and preferred examples thereof are also the same as those described above. Among them, bis(hydroxyphenyl)alkane-based dihydric phenols are preferred, and bisphenol A is more preferred.

The aromatic polycarbonate-based resins may be used alone or in combination thereof. The aromatic polycarbonate resin (B) may have a structure free of such a polyorganosiloxane block as represented by the formula (II) unlike the polycarbonate-polyorganosiloxane copolymer (A). For example, the aromatic polycarbonate-based resin (B) may be a homopolycarbonate resin.

<Styrene-Based Resin (C)>

The styrene-based resin (C) to be used in the polycarbonate-based resin composition of the present invention preferably has constituent units derived from acrylonitrile and styrene, and more preferably has constituent units derived from butadiene, acrylonitrile, and styrene, and an amorphous styrene-based resin and a crystalline styrene-based resin may each be used. In the present invention, one kind of styrene-based resin may be used as the styrene-based resin (C), or two or more kinds of styrene-based resins may be used in combination as the resin.

The blending amount of the styrene-based resin (C) in the polycarbonate-based resin composition is preferably from 1 mass % or more to 50 mass % or less, more preferably from 3 mass % or more to 45 mass % or less, still more preferably from 15 mass % or more to 40 mass % or less, particularly preferably from 20 mass % or more to 35 mass % or less in 100 mass % of the total amount of the polycarbonate-based resin (S) and the styrene-based resin (C) from the viewpoints of improvements in moldability and fluidity of the polycarbonate-based resin composition.

The amorphous styrene-based resin is, for example, a polymer free of any crystal structure obtained by polymerizing a monomer or monomer mixture formed of 20 mass % or more to 100 mass % or less of a monovinylic aromatic monomer, such as styrene or α-methylstyrene, 0 mass % or more to 60 mass % or less of a vinyl cyanide-based monomer, such as acrylonitrile or methacrylonitrile, and 0 mass % or more to 50 mass % or less of any other vinylic monomer copolymerizable with these monomers, such as maleimide or methyl (meth)acrylate.

Examples of such polymer include general-purpose polystyrene (GPPS) and an acrylonitrile-styrene copolymer (AS resin).

In addition, a rubber-modified styrene-based resin reinforced with a rubber-like polymer may be preferably utilized as the amorphous styrene-based resin. The rubber-modified styrene-based resin is preferably an acrylonitrile-butadiene-styrene copolymer, and examples thereof include: high-impact polystyrene (HIPS) obtained by polymerizing a rubber, such as polybutadiene, with styrene; an acrylonitrile-butadiene-styrene copolymer (ABS resin) obtained by polymerizing polybutadiene with acrylonitrile and styrene; and a methyl methacrylate-butadiene-styrene copolymer (MBS resin) obtained by polymerizing polybutadiene with methyl methacrylate and styrene. The rubber-modified styrene-based resins may be used in combination thereof, and may also be used as a mixture with the rubber-unmodified amorphous styrene-based resin.

The content of the rubber in the rubber-modified styrene-based resin is preferably from 2 mass % or more to 50 mass % or less, more preferably from 5 mass % or more to 30 mass % or less, still more preferably from 5 mass % or more to 15 mass % or less. When the content of the rubber is 2 mass % or more, the impact resistance of the composition is sufficient, and when the content is 50 mass % or less, a problem, such as a reduction in thermal stability thereof, a reduction in melt fluidity thereof, the occurrence of gel, or the coloring thereof, does not occur.

Specific examples of the rubber include polybutadiene, a rubbery polymer containing an acrylate and/or a methacrylate, a styrene-butadiene-styrene rubber (SBS), a styrene-butadiene rubber (SBR), a butadiene-acrylic rubber, an isoprene rubber, an isoprene-styrene rubber, an isoprene-acrylic rubber, and an ethylene-propylene rubber. Among them, polybutadiene is particularly preferred. Any one of a polybutadiene having a low 1,4-cis bond content (e.g., a polybutadiene containing 1 mol % or more to 30 mol % or less of a 1,2-vinyl bond and 30 mol % or more to 42 mol % or less of a 1,4-cis bond) and a polybutadiene having a high 1,4-cis bond content (e.g., a polybutadiene containing 20 mol % or less of a 1,2-vinyl bond and 78 mol % or more of a 1,4-cis bond) may be used as the polybutadiene to be used herein. In addition, the polybutadiene may be a mixture thereof.

In addition, the crystalline styrene-based resin is, for example, a styrene-based (co)polymer having a syndiotactic structure or an isotactic structure. In the present invention, however, the amorphous styrene-based resin is preferably used for the purpose of further improving the fluidity of the composition. Further, among the amorphous styrene-based resins, a resin having a melt flow rate (MFR) at 200° C. and a load of 5 kg of preferably from 0.5 g/10 minutes or more to 100 g/10 minutes or less, more preferably from 2 g/10 minutes or more to 80 g/10 minutes or less, still more preferably from 2 g/10 minutes or more to 50 g/10 minutes or less is used. When the melt flow rate (MFR) is 5 g/10 minutes or more, sufficient fluidity is obtained, and when the melt flow rate is 100 g/10 minutes or less, the impact resistance of the polycarbonate-based resin composition becomes satisfactory.

Further, among the amorphous styrene-based resins, a high-impact polystyrene resin (HIPS), an acrylonitrile-styrene copolymer (AS resin), an acrylonitrile-butadiene-styrene copolymer (ABS resin), a methyl methacrylate-styrene copolymer (MS resin), a methyl methacrylate-butadiene-styrene copolymer (MBS resin), an acrylonitrile-methyl acrylate-styrene copolymer (AAS resin), and an acrylonitrile-(ethylene/propylene/diene copolymer)-styrene copolymer (AES resin) are preferred, an acrylonitrile-styrene copolymer (AS resin), an acrylonitrile-butadiene-styrene copolymer (ABS resin), and a methyl methacrylate-butadiene-styrene copolymer (MBS resin) are more preferred, and an acrylonitrile-butadiene-styrene copolymer (ABS resin) and an acrylonitrile-styrene copolymer (AS resin) are still more preferred.

<Other Components>

Any other additive may be incorporated into the polycarbonate-based resin composition of the present invention to the extent that the effects of the present invention are not impaired. Examples of the other additive may include a flame retardant, a flame retardant auxiliary, an antioxidant, a UV absorber, a release agent, a reinforcing material, a filler, an elastomer for an impact resistance improvement, a dye, a pigment, and an antistatic agent.

The polycarbonate-based resin composition of the present invention is obtained by: blending the above-mentioned respective components at the above-mentioned ratios and various optional components to be used as required at appropriate ratios; and kneading the components.

In one aspect of the present invention, the total content of the component (A), the component (B), and the component (C) is preferably from 80 mass % to 100 mass %, more preferably from 95 mass % to 100 mass % with respect to the total amount (100 mass %) of the polycarbonate-based resin composition.

In another aspect of the present invention, the total content of the component (A), the component (B), the component (C), and the other component is preferably from 90 mass % to 100 mass %, more preferably from 95 mass % to 100 mass % with respect to the total amount (100 mass %) of the polycarbonate-based resin composition.

The blending and the kneading may be performed by a method involving premixing with a typically used apparatus, such as a ribbon blender or a drum tumbler, and using, for example, a Henschel mixer, a Banbury mixer, a single-screw extruder, a twin-screw extruder, a multi-screw extruder, or a Ko-kneader. In normal cases, a heating temperature at the time of the kneading is appropriately selected from the range of from 240° C. or more to 320° C. or less. An extruder, in particular a vented extruder is preferably used in the melt-kneading.

[Molded Article]

Various molded bodies may each be produced by an injection molding method, an injection compression molding method, an extrusion molding method, a blow molding method, a press molding method, a vacuum molding method, an expansion molding method, or the like using as a raw material the melt-kneaded polycarbonate-based resin composition of the present invention or a pellet obtained through the melt-kneading. In particular, the pellet obtained through the melt-kneading can be suitably used in the production of injection-molded bodies by injection molding and injection compression molding.

The molded article comprising the polycarbonate-based resin composition of the present invention can be suitably used as, for example: a casing for parts for electrical and electronic equipment, such as a television, a radio, a video camera, a videotape recorder, an audio player, a DVD player, an air conditioner, a cellular phone, a display, a computer, a register, an electronic calculator, a copying machine, a printer, a facsimile, a communication base station, or a battery; or parts for an automobile and a building material.

EXAMPLES

The present invention is more specifically described by way of Examples. However, the present invention is by no means limited by these Examples. In each of Examples, characteristic values and evaluation results were determined in the following manner.

(1) Chain Length and Content of Polydimethylsiloxane

The chain length and content of a polydimethylsiloxane were calculated by NMR measurement from the integrated value ratio of a methyl group of the polydimethylsiloxane. In this description, the polydimethylsiloxane is sometimes abbreviated as “PDMS”.

<Quantification Method for Chain Length of Polydimethylsiloxane>

¹H-NMR Measurement Conditions

NMR apparatus: ECA500 manufactured by JEOL Resonance Co., Ltd.

Probe: TH5 corresponding to 5 φ NMR test tube

Observed range: −5 ppm to 15 ppm

Observation center: 5 ppm

Pulse repetition time: 9 sec

Pulse width: 45°

NMR sample tube: 5 φ

Sample amount: 30 mg to 40 mg

Solvent: deuterochloroform

Measurement temperature: room temperature

Number of scans: 256 times Allylphenol-terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.5

B: an integrated value of a methylene group in allylphenol observed around δ 2.50 to δ 2.75

Chain length of polydimethylsiloxane=(A/6)/(B/4) Eugenol-terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.5

B: an integrated value of a methylene group in eugenol observed around δ 2.40 to δ 2.70

Chain length of polydimethylsiloxane=(A/6)/(B/4)

<Quantification Method for Content of Polydimethylsiloxane>

Quantification method for the copolymerization amount of a polydimethylsiloxane in a PTBP-terminated polycarbonate obtained by copolymerizing an allylphenol-terminated polydimethylsiloxane.

NMR apparatus: ECA-500 manufactured by JEOL Resonance Co., Ltd.

Probe: TH5 corresponding to 5 φ NMR test tube

Observed range: −5 ppm to 15 ppm

Observation center: 5 ppm

Pulse repetition time: 9 sec

Pulse width: 45°

Number of scans: 256 times

NMR sample tube: 5 φ

Sample amount: 30 mg to 40 mg

Solvent: deuterochloroform

Measurement temperature: room temperature

A: an integrated value of a methyl group in a BPA moiety observed around δ 1.5 to δ 1.9

B: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.3

C: an integrated value of a butyl group in a p-tert-butylphenyl moiety observed around δ 1.2 to δ 1.4

a=A/6

b=B/6

c=C/9

T=a+b+c

f=a/T×100

g=b/T×100

h=c/T×100

TW=f×254+g×74.1+h×149

PDMS (wt %)=g×74.1/TW×100

(2) Viscosity-Average Molecular Weight

A viscosity-average molecular weight (Mv) was calculated from the following equation (Schnell's equation) by using a limiting viscosity [η] determined through the measurement of the viscosity of a methylene chloride solution at 20° C. with an Ubbelohde-type viscometer. [η]=1.23×10⁻⁵×Mv^(0.83)

In addition, the viscosity-average molecular weight (Mv) of the polycarbonate-based resin (S) was determined from the value of the arithmetic average of the viscosity-average molecular weights of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B).

<Method of Observing Domain Structure with SPM>

SPM apparatus: Nano-IM (manufactured by PNI)

Probe: PPP-NCHR (manufactured by Nanosensors)

Size of observation field of view: A 1-micrometer square, a 2-micrometer square, or a 5-micrometer square

Observed site: A surface formed of the machine direction (MD) and thickness direction (ND) of the central portion of a section distant from the end portion of an Izod test piece (measuring 63.5 mm long by 12.7 mm wide by 3.2 mm thick) to be described later on a side opposite to a gate by about 5 mm

Pretreatment method: An Izod test piece to be described later was cut, and the resultant cut sample was subjected to surface shaping adjustment. Subsequently, an observation surface was produced by cut section processing with a freezing microtome. Details about the respective procedures are as described below.

[1. Cutting of Izod Test Piece]

The Izod test piece was cut at a position illustrated in FIG. 4 to provide a test piece measuring 7 mm long by 5 mm wide by 3.2 mm thick.

[2. Surface Shaping Adjustment from Cut-Out Sample]

The observation surface side of the test piece obtained in the 1. was trimmed into a quadrangular pyramid shape with a trimming apparatus (“Leica EM TRIM” [manufactured by Leica Microsystems]).

Subsequently, the apices of the quadrangular pyramid were cut off with a microtome (“ULTRACUT S” [manufactured by Leica Microsystems]) at normal temperature so that a surface of about a 150-micrometer square appeared.

The shape of a glass knife used in the microtome is as illustrated in FIG. 6. A “glass rod for a glass knife (length: 400 mm, width: 25 mm, thickness: 6 mm)” [Nisshin EM Co., Ltd., Tokyo] was used as a material, and a glass knife maker (“Leica EM KMR2” [manufactured by Leica Microsystems]) was used as a processing apparatus. The fracture surface of the produced glass knife was observed with a microscope, and such a glass knife that no chip was observed in a side to be used in the cutting was used.

[3. Production of Observation Surface by Cutting with Freezing Microtome]

The sample subjected to the surface shaping in the 2. was placed in a cooling box placed in a freezing microtome (“ULTRACUT R” [manufactured by Leica Microsystems]) together with the glass knife. Liquid nitrogen was used to set an atmospheric temperature in the box to −120° C., and the sample was cooled at the temperature for 1 hour.

Subsequently, the sample was cut out into a surface of from about a 200-micrometer square to about a 500-micrometer square as illustrated in FIG. 5 without being removed from the cooling box. Thus, the observation surface was obtained.

Measurement Mode: A Phase Difference Mode

Domain to be evaluated: A domain whose entirety was reflected in an observation field of view was defined as a domain to be evaluated.

Size of observation field of view to be used in domain evaluation: When the number of domains to be evaluated in the case of observation in a 1-micrometer square was 21 or more, the 1-micrometer square was defined as the size of an observation field of view to be used in a domain evaluation, when the number was from 6 or more to 20 or less, a 2-micrometer square was defined as the size of the observation field of view to be used in the domain evaluation, and when the number was 5 or less, a 5-micrometer square was defined as the size of the observation field of view to be used in the domain evaluation.

Number of domains to be observed: The observation number of domains to be evaluated to be used in the calculation of the ratio of the number of the domains (d), the average sectional area of the domains, and the average of distances between the adjacent particles of the domains was set to 70 or more. When the number of domains to be evaluated per one observation field of view was less than 70, additional observation was performed until the number became 70 or more.

Image analysis software: SPIP

An acrylonitrile-butadiene-styrene resin (hereinafter sometimes referred to as “ABS”) and an acrylonitrile-styrene resin (hereinafter sometimes referred to as “AS”) are incompatible with the polycarbonate-based resin (S), and hence such a domain formed of the ABS or the AS as shown in each of FIG. 7 and FIG. 18 is formed in a matrix formed of the polycarbonate-based resin (S). The feature of the ABS domain lies in that a butadiene block is spherically dispersed in the AS. There is no large difference in physical property (viscoelasticity) between the AS and the matrix formed of the polycarbonate-based resin (S), and hence an interface between the domain formed of the ABS or the AS and the matrix is unclear. However, the domain is characterized in that the domain shows a contour as if there were a difference in height between the domain and the matrix even in a phase difference image. The domain formed of the ABS or the AS undergoes a phase separation from the polycarbonate-based resin (S), and hence a site in which no domain formed of the ABS or the AS is present needs to be subjected to the measurement for observing the domain (d) present in the aromatic polycarbonate-based resin (B).

Accordingly, first, SPM measurement was performed in a wide field of view measuring about 10 μm by about 10 μm to confirm a region free of any domain formed of the ABS or the AS. After that, the region was observed in an extended field of view (1 μm by 1 μm or 2 μm by 2 μm).

<Judgment of Presence/Absence of Domain (d) with SPM, and Methods of Calculating Number of Domains (d-2) Inside Domain (d-1) and Ratio of Number of Domains (d) to Total Number of all Domains>

The number of all domains to be evaluated was automatically calculated with the SPIP, and the number of the domains (d) was visually counted.

<Method of Calculating Average Sectional Area of Domains with SPM>

The sectional areas of the respective domains were automatically calculated by subjecting the domains to image processing with the SPIP, and their average was calculated.

<Method of Calculating Average of Distances Between Adjacent Particles with SPM>

Distances between the adjacent particles of the respective domains were automatically calculated with the SPIP, and their average was calculated.

<Production of Polycarbonate Oligomer>

Sodium dithionite was added in an amount of 2,000 ppm with respect to bisphenol A (BPA) (to be dissolved later) to 5.6 mass % aqueous sodium hydroxide, and then BPA was dissolved in the mixture so that the concentration of BPA was 13.5 mass %. Thus, a solution of BPA in aqueous sodium hydroxide was prepared. The solution of BPA in aqueous sodium hydroxide, methylene chloride, and phosgene were continuously passed through a tubular reactor having an inner diameter of 6 mm and a tube length of 30 m at flow rates of 40 L/hr, 15 L/hr, and 4.0 kg/hr, respectively. The tubular reactor had a jacket portion and the temperature of the reaction liquid was kept at 40° C. or less by passing cooling water through the jacket. The reaction liquid that had exited the tubular reactor was continuously introduced into a baffled vessel type reactor provided with a swept back blade and having an internal volume of 40 L. The solution of BPA in aqueous sodium hydroxide, 25 mass % aqueous sodium hydroxide, water, and a 1 mass % aqueous solution of triethylamine were further added to the reactor at flow rates of 2.8 L/hr, 0.07 L/hr, 17 L/hr, and 0.64 L/hr, respectively, to perform a reaction. An aqueous phase was separated and removed by continuously taking out the reaction liquid overflowing the vessel type reactor and leaving the reaction liquid at rest. Then, a methylene chloride phase was collected.

The polycarbonate oligomer thus obtained had a concentration of 341 g/L and a chloroformate group concentration of 0.71 mol/L.

Production Example 1

<PC-POS Copolymer (A-1a)>

Values for the following (i) to (xiv) are as shown in Table 1.

(i) L of the polycarbonate oligomer solution (PCO) produced as described above, (ii) L of methylene chloride (MC), a solution obtained by dissolving (iv) g of an allylphenol terminal-modified polydimethylsiloxane having an average chain length “n” of (iii) in (v) L of methylene chloride (MC), and (vi) mL of triethylamine (TEA) were loaded into a 50-liter vessel-type reactor including a baffle board, a paddle-type stirring blade, and a cooling jacket. (vii) g of 6.4 mass % aqueous sodium hydroxide (NaOHaq) was added to the mixture under stirring, and a reaction between the polycarbonate oligomer and the allylphenol terminal-modified PDMS was performed for 20 minutes.

A solution of p-tert-butylphenol (PTBP) in methylene chloride (obtained by dissolving (viii) g of PTBP in (ix) L of methylene chloride (MC)) and a solution of BPA in aqueous sodium hydroxide (obtained by dissolving (xiii) g of BPA in an aqueous solution obtained by dissolving (x) g of NaOH and (xi) g of sodium dithionite (Na₂S₂O₄) in (xii) L of water) were added to the polymerization liquid, and the mixture was subjected to a polymerization reaction for 40 minutes.

(xiv) L of methylene chloride (MC) was added to the resultant for dilution, and the mixture was stirred for 10 minutes. After that, the mixture was separated into an organic phase containing a PC-POS, and an aqueous phase containing excess amounts of BPA and NaOH, and the organic phase was isolated.

A solution of the PC-POS in methylene chloride thus obtained was sequentially washed with 0.03 mol/L aqueous NaOH and 0.2 mol/L hydrochloric acid in amounts of 15 vol % each with respect to the solution. Next, the solution was repeatedly washed with pure water until an electric conductivity in an aqueous phase after the washing became 0.01 ρS/m or less.

The solutions of the polycarbonates in methylene chloride obtained by the washing were concentrated and pulverized, and the resultant flakes were dried under reduced pressure at 120° C. to provide PC-POS copolymers (A1) to (A17). The resultant flake was subjected to the measurement of a PDMS content, an unreacted PDMS amount, and a viscosity-average molecular weight.

Production Example 2

<PC-POS Copolymer (A-1b)>

Production and measurement were performed in the same manner as in Production Example 1 except that the values (i) to (xiv) were changed as described in Table 1.

TABLE 1 Production Production Example 1 Example 2 PC-POS (A) A-1a A-1b (i) PCO (L) 11 11 (ii) MC (L) 24.5 24.5 (iii) PDMS chain length (n) 61 88 (iv) PDMS loading amount (g) 1,800 1,400 (v) MC (L) 2.0 2.0 (vi) TEA (mL) 6.2 6.2 (vii) NaOHaq (g) 1,405 937 (viii) PTBP (g) 107.6 107.6 (ix) MC (L) 0.5 0.5 (x) NaOH (g) 412 412 (xi) Na₂S₂O₄ (g) 1.5 1.5 (xii) Water (L) 6.0 6.0 (xiii) BPA (g) 766 766 (xiv) MC (L) 0 0 PDMS content (wt %) 30 25 Unreacted PDMS amount (ppm) ≤150 ≤150 Mv 17,700 17,700 <PC-POS Copolymer (A-2)>

PC-POS copolymer A-2a: “FG1700” [PC-POS copolymer, polyorganosiloxane block chain length: 88, polyorganosiloxane content: 6 mass %, viscosity-average molecular weight Mv: 17,700]

<Aromatic Polycarbonate-Based Resin (B)>

Aromatic polycarbonate-based resin B-1: “FN2500” [viscosity-average molecular weight Mv: 23,500]

Aromatic polycarbonate-based resin B-2: “FN2200” [viscosity-average molecular weight Mv: 21,300]

Aromatic polycarbonate-based resin B-3: “FN1900” [viscosity-average molecular weight Mv: 19,300]

Aromatic polycarbonate-based resin B-4: “FN1700” [viscosity-average molecular weight Mv: 17,700]

<Styrene-Based Resin (C)>

“KRALASTIC SXH-330” [acrylonitrile-butadiene-styrene terpolymer (ABS), manufactured by Kumho Petrochemical Co., Ltd., content of constituent unit derived from butadiene: 60 mass %]

“SANTAC AT-05” [acrylonitrile-butadiene-styrene terpolymer (ABS), manufactured by Nippon A & L Inc., content of constituent unit derived from butadiene: 14 mass %]

“KIBISAN PN-117C” [acrylonitrile-styrene copolymer (AS), manufactured by Chimei Corporation, content of constituent unit derived from acrylonitrile: 24 mass %]

<Other Component>

Antioxidant: “IRGAFOS 168 (product name)” [tris(2,4-di-tert-butylphenyl) phosphite, manufactured by BASF Japan]

Antioxidant: “IRGANOX 1076 (product name)” [octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, manufactured by BASF Japan]

Reference Examples 1 and 2, Examples 1 to 27, and Comparative Examples 1 to 22

The PC-POS copolymers A-1a and A-1b obtained in Production Examples 1 and 2, and the other respective components were mixed at blending ratios shown in Table 2 to Table 6. Each of the mixtures was supplied to a vented twin-screw extruder (manufactured by Toshiba Machine Co., Ltd., TEM-35B), and was melt-kneaded at a screw revolution number of 150 rpm, an ejection amount of 20 kg/hr, and a resin temperature of from 295° C. to 300° C. to provide an evaluation pellet sample. Image observation and image analysis with the SPM were performed by using the evaluation pellet sample. Typical images (the images each correspond to a 1-micrometer square) of the results of the observation of the respective inorganic-filler containing polycarbonate resin compositions obtained in Reference Examples 1 and 2, Examples 1 to 27, and Comparative Examples 1 to 22 with the SPM are shown in FIG. 8 to FIG. 17 and FIG. 19 to FIG. 22.

TABLE 2 Reference Reference Example Comparative Example Example Comparative Example 1 Example 2 1 Example 1 2 3 Example 2 A-1 A-1a (Production parts by mass 8 11.2 14 Example 1) A-1b (Production parts by mass 9.6 16.8 Example 2) A-2 FG1700 parts by mass 56 70 B B-1 (FN2500) parts by mass B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass 7 7 B-4 (FN1700) parts by mass 92 90.4 58.8 14 49 46.2 C SXH-330 parts by mass 30 30 30 30 30 SANTAC AT-05 parts by mass PN-117C parts by mass Other Irgafos 168 parts by mass 0.05 0.05 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 2.4 2.4 4.8 4.8 6.0 6.0 6.0 content in PC-based resin (S) Viscosity-average molecular — 17,700 17,700 17,700 17,700 17,700 17,700 17,700 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % — — — — 56 — 0 total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 2,449 888 — — 1,755 — 785 domains Average distance of distances nm 155 77 — — 100 — 71 between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 21 22 20 20 20 Q value (280° C., 160 kg) ×0.01 ml/s 13 13 58 63 63 63 64 Izod impact strength (23° C.) kJ/m² 73 74 73 68 84 84 65 Izod impact strength (0° C.) kJ/m² — — — — — Izod impact strength (−10° C.) kJ/m² — — — — — Izod impact strength (−20° C.) kJ/m² — — — — — Izod impact strength (−30° C.) kJ/m² 57 46 76 70 46 Izod impact strength (−40° C.) kJ/m² 54 53 51 35 70 65 40 Deflection temperature under ° C. 128 128 111 111 108 108 109 load Example Comparative Example Example Comparative 4 Example 3 5 6 Example 4 A-1 A-1a (Production parts by mass 2.8 4.2 Example 1) A-1b (Production parts by mass 5 Example 2) A-2 FG1700 parts by mass 14 21 B B-1 (FN2500) parts by mass 22 38 25 25 49 B-2 (FN2200) parts by mass 45.2 18 40.8 40 B-3 (FN1900) parts by mass B-4 (FN1700) parts by mass C SXH-330 parts by mass 30 30 30 30 30 SANTAC AT-05 parts by mass PN-117C parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 1.2 1.2 1.8 1.8 1.8 content in PC-based resin (S) Viscosity-average molecular — 21,800 21,800 21,800 21,800 21,800 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 16 1 65 63 — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 1,373 445 1,118 848 — domains Average distance of distances nm 109 91 114 101 — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 14 14 14 13 14 Q value (280° C., 160 kg) ×0.01 ml/s 40 42 38 39 39 Izod impact strength (23° C.) kJ/m² 91 93 109 91 106 Izod impact strength (0° C.) kJ/m² — — — — — Izod impact strength (−10° C.) kJ/m² — — — — — Izod impact strength (−20° C.) kJ/m² — — — — — Izod impact strength (−30° C.) kJ/m² 50 40 52 55 43 Izod impact strength (−40° C.) kJ/m² 40 29 40 40 30 Deflection temperature under ° C. 114 114 113 113 113 load

TABLE 3 Example Comparative Example Comparative 7 Example 5 8 Example 6 A-1 A-1a (Production parts by mass 3 4.5 Example 1) A-1b (Production parts by mass Example 2) A-2 FG1700 parts by mass 15 23 B B-1 (FN2500) parts by mass B-2 (FN2200) parts by mass 30 38 31 44 B-3 (FN1900) parts by mass 42 22 39.5 8 B-4 (FN1700) parts by mass C SXH-330 parts by mass 25 25 25 25 SANTAC AT-05 parts by mass PN-117C parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 1.2 1.2 1.8 1.8 content in PC-based resin (S) Viscosity-average molecular — 20,000 20,000 20,100 20,000 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 74 0 — — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 2,188 187 — — domains Average distance of distances nm 137 77 — — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 18 18 17 17 Q value (280° C., 160 kg) ×0.01 ml/s 37 37 35 38 Izod impact strength (23° C.) kJ/m² 76 75 77 77 Izod impact strength (0° C.) kJ/m² — — — — Izod impact strength (−10° C.) kJ/m² — — — — Izod impact strength (−20° C.) kJ/m² — — — — Izod impact strength (−30° C.) kJ/m² 50 31 59 50 Izod impact strength (−40° C.) kJ/m² 27 23 43 27 Deflection temperature under ° C. 117 118 116 117 load Example Example Comparative 9 10 Example 7 A-1 A-1a (Production parts by mass 6 Example 1) A-1b (Production parts by mass 7.2 Example 2) A-2 FG1700 parts by mass 30 B B-1 (FN2500) parts by mass 5 B-2 (FN2200) parts by mass 32 32.8 40 B-3 (FN1900) parts by mass 37 35.0 B-4 (FN1700) parts by mass C SXH-330 parts by mass 25 25 25 SANTAC AT-05 parts by mass PN-117C parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 Polyorganosiloxane block mass % 2.4 2.4 2.4 content in PC-based resin (S) Viscosity-average molecular — 20,000 20,000 20,000 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 35 7 0 total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 1,781 396 606 domains Average distance of distances nm 137 85 72 between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 17 16 17 Q value (280° C., 160 kg) ×0.01 ml/s 35 37 33 Izod impact strength (23° C.) kJ/m² 77 77 78 Izod impact strength (0° C.) kJ/m² — — — Izod impact strength (−10° C.) kJ/m² — — — Izod impact strength (−20° C.) kJ/m² — — — Izod impact strength (−30° C.) kJ/m² 59 58 57 Izod impact strength (−40° C.) kJ/m² 43 47 35 Deflection temperature under ° C. 116 117 116 load Example Comparative Example Comparative 11 Example 8 12 Example 9 A-1 A-1a (Production parts by mass 7.5 7.2 Example 1) A-1b (Production parts by mass Example 2) A-2 FG1700 parts by mass 38 36 B B-1 (FN2500) parts by mass 17 B-2 (FN2200) parts by mass 34 20 B-3 (FN1900) parts by mass 33.5 5 B-4 (FN1700) parts by mass 77.8 54 C SXH-330 parts by mass 25 25 10 10 SANTAC AT-05 parts by mass PN-117C parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 3.0 3.0 2.4 2.4 content in PC-based resin (S) Viscosity-average molecular — 20,000 20,000 17,800 17,700 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 71 0 11 0 total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 3,457 249 841 773 domains Average distance of distances nm 139 64 106 91 between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 17 16 23 23 Q value (280° C., 160 kg) ×0.01 ml/s 33 34 21 22 Izod impact strength (23° C.) kJ/m² 77 76 74 74 Izod impact strength (0° C.) kJ/m² — — — — Izod impact strength (−10° C.) kJ/m² — — — — Izod impact strength (−20° C.) kJ/m² — — — — Izod impact strength (−30° C.) kJ/m² 63 59 61 62 Izod impact strength (−40° C.) kJ/m² 60 39 59 37 Deflection temperature under ° C. 115 116 123 123 load Example Comparative 13 Example 10 A-1 A-1a (Production parts by mass 7.5 Example 1) A-1b (Production parts by mass Example 2) A-2 FG1700 parts by mass 37.5 B B-1 (FN2500) parts by mass 17.5 B-2 (FN2200) parts by mass 35.5 20 B-3 (FN1900) parts by mass 32 B-4 (FN1700) parts by mass C SXH-330 parts by mass SANTAC AT-05 parts by mass 25 25 PN-117C parts by mass Other Irgafos 168 parts by mass 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 Polyorganosiloxane block mass % 3.0 3.0 content in PC-based resin (S) Viscosity-average molecular — 20,100 20,000 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 23 — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 629 — domains Average distance of distances nm 106 — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 22 22 Q value (280° C., 160 kg) ×0.01 ml/s 46 47 Izod impact strength (23° C.) kJ/m² 80 75 Izod impact strength (0° C.) kJ/m² — — Izod impact strength (−10° C.) kJ/m² — — Izod impact strength (−20° C.) kJ/m² — — Izod impact strength (−30° C.) kJ/m² 60 53 Izod impact strength (−40° C.) kJ/m² 41 35 Deflection temperature under load ° C. 116 116

TABLE 4 Example Example Comparative Comparative 14 15 Example 11 Example 12 A-1 A-1a (Production parts by mass 9.6 Example 1) A-1b (Production parts by mass 11.5 Example 2) A-2 FG1700 parts by mass 48 B B-1 (FN2500) parts by mass 32 32 32 25 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass 55 B-4 (FN1700) parts by mass 38.4 36.5 C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 20 20 20 20 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 3.6 3.6 3.6 0.0 content in PC-based resin (S) Viscosity-average molecular — 20,000 20,000 20,000 22,000 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 81 88 — — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 5,078 2,069 — — domains Average distance of distances nm 141 88 — — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 16 16 17 23 Q value (280° C., 160 kg) ×0.01 ml/s 36 36 39 38 Izod impact strength (23° C.) kJ/m² 71 50 34 6 Izod impact strength (0° C.) kJ/m² 58 49 35 6 Izod impact strength (−10° C.) kJ/m² 54 46 14 6 Izod impact strength (−20° C.) kJ/m² 53 40 14 6 Izod impact strength (−30° C.) kJ/m² 45 21 13 — Izod impact strength (−40° C.) kJ/m² — — — — Deflection temperature under ° C. 117 118 117 121 load Example Example Comparative Comparative 16 17 Example 13 Example 14 A-1 A-1a (Production parts by mass 12.8 Example 1) A-1b (Production parts by mass 15.4 Example 2) A-2 FG1700 parts by mass 64 B B-1 (FN2500) parts by mass 16 16 16 B-2 (FN2200) parts by mass 60 B-3 (FN1900) parts by mass 20 B-4 (FN1700) parts by mass 51.2 48.6 C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 20 20 20 20 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 4.8 4.8 0.0 content in PC-based resin (S) Viscosity-average molecular — 18,900 18,900 18,900 20,800 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % — — — — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² — — — — domains Average distance of distances nm — — — — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 18 18 18 27 Q value (280° C., 160 kg) ×0.01 ml/s 41 45 45 42 Izod impact strength (23° C.) kJ/m² 65 48 24 6 Izod impact strength (0° C.) kJ/m² 62 46 26 6 Izod impact strength (−10° C.) kJ/m² 61 44 14 6 Izod impact strength (−20° C.) kJ/m² 61 39 14 6 Izod impact strength (−30° C.) kJ/m² 60 32 13 — Izod impact strength (−40° C.) kJ/m² — — — — Deflection temperature under ° C. 116 117 115 120 load

TABLE 5 Example Example Comparative Example 18 19 Example 15 20 A-1 A-1a (Production parts by mass 5.1 10.2 Example 1) A-1b (Production parts by mass 6.1 Example 2) A-2 FG1700 parts by mass 25.5 B B-1 (FN2500) parts by mass 35 B-2 (FN2200) parts by mass 44.5 44.5 44.5 B-3 (FN1900) parts by mass 15 15 15 B-4 (FN1700) parts by mass 20.4 19.4 39.8 C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 15 15 15 15 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 1.8 1.8 1.8 3.6 content in PC-based resin (S) Viscosity-average molecular — 19,900 19,900 19,900 20,100 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % — — — 71 total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² — — — 5,710 domains Average distance of distances nm — — — 140 between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 18 18 17 15 Q value (280° C., 160 kg) ×0.01 ml/s 25 26 25 24 Izod impact strength (23° C.) kJ/m² 73 65 62 78 Izod impact strength (0° C.) kJ/m² 56 50 14 — Izod impact strength (−10° C.) kJ/m² 39 29 13 — Izod impact strength (−20° C.) kJ/m² 19 15 12 83 Izod impact strength (−30° C.) kJ/m² — — — 54 Izod impact strength (−40° C.) kJ/m² — — — 37 Deflection temperature under ° C. 122 122 122 121 load Example Comparative Comparative 21 Example 16 Example 17 A-1 A-1a (Production parts by mass Example 1) A-1b (Production parts by mass 12.2 Example 2) A-2 FG1700 parts by mass 51 B B-1 (FN2500) parts by mass 34 B-2 (FN2200) parts by mass 44.5 26 B-3 (FN1900) parts by mass 15 59 B-4 (FN1700) parts by mass 13.3 C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 15 15 15 Other Irgafos 168 parts by mass 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 Polyorganosiloxane block mass % 3.6 3.6 0.0 content in PC-based resin (S) Viscosity-average molecular — 19,900 20,000 19,900 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % — 0 — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² — 323 — domains Average distance of distances nm — 66 — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 15 14 21 Q value (280° C., 160 kg) ×0.01 ml/s 24 24 24 Izod impact strength (23° C.) kJ/m² 74 63 7 Izod impact strength (0° C.) kJ/m² 63 — 7 Izod impact strength (−10° C.) kJ/m² 58 — 7 Izod impact strength (−20° C.) kJ/m² 57 62 7 Izod impact strength (−30° C.) kJ/m² 45 17 — Izod impact strength (−40° C.) kJ/m² 21 15 — Deflection temperature under ° C. 120 121 124 load

TABLE 6 Example Example Comparative Comparative Example Example 22 23 Example 18 Example 19 24 25 A-1 A-1a (Production parts by mass 5.4 10.8 Example 1) A-1b (Production parts by mass 6.5 13 Example 2) A-2 FG1700 parts by mass 27 B B-1 (FN2500) parts by mass B-2 (FN2200) parts by mass 47 47 47 28 45.2 43 B-3 (FN1900) parts by mass 16 16 16 62 34 34 B-4 (FN1700) parts by mass 21.6 20.5 C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 10 10 10 10 10 10 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 1.8 1.8 1.8 0.0 3.6 3.6 content in PC-based resin (S) Viscosity-average molecular — 19,900 19,900 19,900 19,900 20,100 20,000 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % — — — — 86 53 total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² — — — — 1,861 790 domains Average distance of distances nm — — — — 108 94 between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 17 16 16 19 13 13 Q value (280° C., 160 kg) ×0.01 ml/s 16 16 16 16 15 15 Izod impact strength (23° C.) kJ/m² 84 76 78 9 85 81 Izod impact strength (0° C.) kJ/m² 73 62 62 9 — — Izod impact strength (−10° C.) kJ/m² 63 38 19 9 — — Izod impact strength (−20° C.) kJ/m² 38 17 16 9 86 82 Izod impact strength (−30° C.) kJ/m² 20 15 16 — 70 60 Izod impact strength (−40° C.) kJ/m² — — — — 61 52 Deflection temperature under ° C. 124 125 124 126 124 124 load Comparative Example Example Comparative Comparative Example 20 26 27 Example 21 Example 22 A-1 A-1a (Production parts by mass 9.5 Example 1) A-1b (Production parts by mass 11.4 Example 2) A-2 FG1700 parts by mass 54 47.5 B B-1 (FN2500) parts by mass 36 22.5 B-2 (FN2200) parts by mass 45.5 43.6 25 29 B-3 (FN1900) parts by mass 40 40 66 B-4 (FN1700) parts by mass C SXH-330 parts by mass SANTAC AT-05 parts by mass PN-117C parts by mass 10 5 5 5 5 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 3.6 3.0 3.0 3.0 0.0 content in PC-based resin (S) Viscosity-average molecular — 20,000 20,100 20,000 20,000 19,900 weight (Mv) of PC-based resin (S) Ratio of number of domains (d^(C)) to % 0 55 6 — — total number of domains (d^(C)) and (d′^(C)) Average sectional area of all nm² 245 4,190 468 — — domains Average distance of distances nm 63 131 60 — — between adjacent particles of all domains MFR (300° C., 1.2 kg) g/10 min 13 12 12 12 18 Q value (280° C., 160 kg) ×0.01 ml/s 15 10 10 10 11 Izod impact strength (23° C.) kJ/m² 83 85 88 87 69 Izod impact strength (0° C.) kJ/m² — — — — 14 Izod impact strength (−10° C.) kJ/m² 67 — — — 12 Izod impact strength (−20° C.) kJ/m² 59 87 87 — 10 Izod impact strength (−30° C.) kJ/m² 47 74 67 64 10 Izod impact strength (−40° C.) kJ/m² 22 62 58 30 9 Deflection temperature under ° C. 122 127 127 126 128 load [Evaluation Test] <Fluidity Evaluation> (MFR)

The amount (g/10 min) of a molten resin flowing out of a die having a diameter of 2.095±0.005 mm and a length of 8.000±0.025 mm was measured by using the above-mentioned pellet in conformity with JIS K 7210-1:2014 at 300° C. under a load of 1.2 kg.

<Q Value (Flow Value) [Unit; 10⁻² mL/Sec]>

The amount (mL/sec) of a molten resin flowing out of a nozzle having a diameter of 1.00 mm and a length of 10.00 mm was measured by using the above-mentioned pellet and a Koka flow tester in conformity with JIS K 7210-1:2014: Appendix JA at 280° C. under a pressure of 160 kgf. A Q value represents an outflow amount per unit time, and a higher numerical value therefor means that the fluidity of the resin is better.

<Impact Resistance>

The pellet obtained in the foregoing was dried at 120° C. for 8 hours, and was then subjected to injection molding with an injection molding machine (manufactured by Nissei Plastic Industrial Co., Ltd., NEX110, screw diameter: 36 mmφ) at a cylinder temperature of 280° C. and a die temperature of 80° C. to produce an Izod test piece (length: 63.5 mm, width: 12.7 mm, thickness: 3.2 mm). Notched Izod impact strengths at −40° C., −30° C., −20° C., −10° C., 0° C., and 23° C. were measured by using a test piece obtained by making a notch (r=0.25 mm±0.05 mm) in the test piece through post-processing in conformity with ASTM Standard D-256.

<Deflection Temperature Under Load (Unit; ° C.)>

The pellet obtained in the foregoing was dried at 120° C. for 8 hours, and was then subjected to injection molding with an injection molding machine (manufactured by Nissei Plastic Industrial Co., Ltd., NEX110, screw diameter: 36 mmφ) at a cylinder temperature of 280° C. and a die temperature of 80° C. to provide a test piece (length: 127 mm, width: 12.7 mm, thickness: 3.2 mm). A load of 1.8 MPa was applied to the test piece in conformity with ASTM Standard D-648 at a rate of temperature increase of 120° C./h and a fulcrum-to-fulcrum distance of 100 mm, and the temperature at which the deflection of the test piece measured in an edgewise manner reached 0.26 mm was recorded.

INDUSTRIAL APPLICABILITY

The polycarbonate-based resin composition obtained in the present invention is excellent in impact resistance and is excellent in fluidity. The molded article obtained by molding the polycarbonate-based resin composition can be suitably used as a casing and the like for parts for electrical and electronic equipment, and a part and the like for an automobile and a building material. 

The invention claimed is:
 1. A polycarbonate-based resin composition, comprising: 50 mass % or more to 99 mass % or less of a polycarbonate-based resin (S) containing a polycarbonate-polyorganosiloxane copolymer (A) containing a polycarbonate block (A-1) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (A-2) containing a repeating unit represented by the following general formula (II), and an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and 1 mass % or more to 50 mass % or less of a styrene-based resin (C), wherein the polycarbonate-based resin composition has a structure in which a domain (d^(C)-1) containing the polyorganosiloxane block (A-2) is present in a matrix containing the aromatic polycarbonate-based resin (B) as a main component, and a domain (d^(C)-2) containing at least one selected from the group consisting of the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1) is present inside the domain (d^(C)-1), and wherein a ratio of a number of domains (d^(C)) in each of which the domain (d^(C)-2) is present inside the domain (d^(C)-1) to a total number of the domains (d^(C)) and domains (d′^(C)) each formed only of the domain (d^(C)-1) is from 5% or more to 90% or less:

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4 wherein the viscosity-average molecular weight of the polycarbonate-based resin (S) is 9,000 or more and 23,000 or less; wherein the content of the polyorganosiloxane block (A-2) in the PC-POS copolymer (A) is 21 mass % or more and 70 mass % or less; wherein all domains corresponding to a total of the domains (d^(C)) and the domains (d′^(C)) have an average sectional area of 200 nm² or more and 6,000 nm² or less; wherein the polyorganosiloxane block (A-2) has an average chain length of from 55 or more to 120 or less.
 2. The polycarbonate-based resin composition according to claim 1, wherein a mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) in the polycarbonate-based resin (S) is from 0.1/99.9 to 99.9/0.1.
 3. The polycarbonate-based resin composition according to claim 1, wherein the aromatic polycarbonate-based resin (B) contains a polycarbonate block including, in a main chain thereof, a repeating unit represented by the following general formula (III):

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to
 4. 4. The polycarbonate-based resin composition according to claim 1, wherein the domain or (d^(C)-1) is mainly formed of the polyorganosiloxane block (A-2).
 5. The polycarbonate-based resin composition according to claim 1, wherein the domain (d^(C)-2) is mainly formed of at least one selected from the group consisting of the aromatic polycarbonate-based resin (B) and the polycarbonate block (A-1).
 6. The polycarbonate-based resin composition according to claim 1, wherein only the one domain (d^(C)-2) is present inside the domain (d^(C)-1).
 7. The polycarbonate-based resin composition according to claim 1, wherein the two or more domains (d^(C)-2) are present inside the domain (d^(C)-1).
 8. The polycarbonate-based resin composition according to claim 1, wherein all domains corresponding to a total of the domains (d^(c)) and the domains (d′^(c)) have an average sectional area of 300 nm² or more.
 9. The polycarbonate-based resin composition according to claim 1, wherein an average of distances between adjacent particles of all domains corresponding to a total of the domains (d^(c)) and the domains (d′^(c)) is 500 nm or less.
 10. The polycarbonate-based resin composition according to claim 1, wherein an average of distances between adjacent particles of all domains corresponding to a total of the domains (d^(c)) and the domains (d′^(c)) is 50 nm or more.
 11. The polycarbonate-based resin composition according to claim 1, wherein the polyorganosiloxane block (A-2) has an average chain length of from 60 or more to 120 or less.
 12. The polycarbonate-based resin composition according to claim 1, wherein the content of the polyorganosiloxane block (A-2) in the polycarbonate-polyorganosiloxane copolymer (A) is from 25 mass % or more to 50 mass % or less.
 13. The polycarbonate-based resin composition according to claim 1, wherein a content of the polyorganosiloxane block (A-2) in the polycarbonate-based resin (S) is from 0.1 mass % or more to 10 mass % or less.
 14. The polycarbonate-based resin composition according to claim 1, wherein the polycarbonate-polyorganosiloxane copolymer (A) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.
 15. The polycarbonate-based resin composition according to claim 1, wherein the polycarbonate-based resin (S) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 20,000 or less.
 16. The polycarbonate-based resin composition according to claim 1, wherein the styrene-based resin (C) has constituent units derived from acrylonitrile and styrene.
 17. The polycarbonate-based resin composition according to claim 1, wherein the styrene-based resin (C) comprises at least one selected from an acrylonitrile-butadiene-styrene copolymer and an acrylonitrile-styrene copolymer.
 18. A molded article, which is obtained by molding the polycarbonate-based resin composition of claim
 1. 19. The molded article according to claim 18, wherein the molded article comprises a casing for electrical or electronic equipment.
 20. The molded article according to claim 18, wherein the molded article comprises parts for an automobile or a building material.
 21. The polycarbonate-based resin composition according to claim 1, wherein the content of the polycarbonate-polyorganosiloxane copolymer (A) in the polycarbonate-based resin (S) is 3 mass % or more and 25 mass % or less.
 22. The polycarbonate-based resin composition according to claim 1, wherein the blending amount of the styrene-based resin (C) in the polycarbonate-based resin composition is 3 mass % or more and 45 mass % or less in 100 mass % of the total amount of the polycarbonate-based resin (S) and the styrene-based resin (C).
 23. The polycarbonate-based resin composition according to claim 1, wherein “a” and “b” in the general formula (I) each represent 0, X in the general formula (I) represents a single bond or an alkylene group having 1 to 8 carbon atoms, and R³ and R⁴ in the general formula (II) each represent a methyl group.
 24. The polycarbonate-based resin composition according to claim 1, wherein the content of the polycarbonate-polyorganosiloxane copolymer (A) in the polycarbonate-based resin (S) is 3 mass % or more and 25 mass % or less, wherein the blending amount of the styrene-based resin (C) in the polycarbonate-based resin composition is 3 mass % or more and 45 mass % or less in 100 mass % of the total amount of the polycarbonate-based resin (S) and the styrene-based resin (C), wherein “a” and “b” in the general formula (I) each represent 0, X in the general formula (I) represents a single bond or an alkylene group having 1 to 8 carbon atoms, and R³ and R⁴ in the general formula (II) each represent a methyl group. 